Polymer Property : Tensile Modulus = 8.96 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D638
Quantum PEEK 30% Glass Fiber Filled
Information provided by Quantum Advanced Engineering Plastics
Tensile Modulus 8.96 GPa
1300 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® PK-15CF-15GB/000 Polyetheretherketone (PEEK), Glass Bead, Carbon Fiber Reinforced  (discontin
Description/Features:Carbon Fiber ReinforcedGlass Bead FilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Modulus 8.96 GPa
1300 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® RA-13CF/000 Polyarylsulfone, Carbon Fiber Reinforced  (discontinued **)
Carbon Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Modulus 8.96 GPa
1300 ksi
5 mm/min; ASTM D638
LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant  (discontinued **)
Office equipment internal parts.Features: Lubricated, Good Wear ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labe..
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D638
Solvay Specialty Polymers Supradel® HTS-2430 High Temperature Sulfone Resin  (discontinued **)
SUPRADEL HTS-2420 is a 20% glass-fiber reinforced high-temperature, high-performance, amorphous, sulfone polymer. With a glass transition temperature of 245°C and a heat deflection temperature of ..
Tensile Modulus 8.96 GPa
1300 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific)
30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Modulus 8.96 GPa
1300 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM CRS5311 PEI (Asia Pacific)
30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing.
Tensile Modulus 8.96 GPa
1300 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon WFD059 PBT (Asia Pacific)
LNP* Stat-kon* WFD059 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.This data was supplied ..
Tensile Modulus 8.96 GPa
1300 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific)
LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D638
Ensinger Tecapeek® PVX Polyetheretherketone (PEEK)
TECAPEEK® PVX is an ultra high performance bearing material made from Victrex® PEEK polymer. TECAPEEK® PVX incorporates the properties of a premium polymetric matrix material with optimum levels..
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D638
Applied Nanostructured Solutions Carbon NanoStructure Chopped Fiber
Carbon NanoStructure (CNS) Chopped Fiber begins as a single-end glass roving product, such as E-CR glass, that is enhanced using a proprietary ANS process. Unique multiwall carbon nanotube-based CNS..
Tensile Modulus 8.96 GPa
1300 ksi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® ATH-25GF/000 Acetal-Homopolymer, Glass Filled  (discontinued **)
Description/Features:Glass Fiber ReinforcedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
Tensile Modulus 8.96 GPa
1300 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermotuf WF006I Polyester, TP
LNP THERMOTUF* WF006I is a compound based on Polyester, TP resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas reg..