Polymer Property : Film Tensile Strength at Break, TD = 2180 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 527
Premix Thermoplastics PRE-ELEC® CP 1317 PRE-ELEC CP 1317 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1317 ..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 527
Premix Thermoplastics PRE-ELEC® CP 1319 PRE-ELEC CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1319 ..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
SABIC HP4023W Low Density Polyethylene for Blown Film Product Description: HP4023W is a Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It yields excellent processability with goo..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 0.5 mil Film (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer, good clarity, laundry and dry cleaning film resin capable of providing a tough film in very thin gauges.Applications: Dry cleaning es..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
ExxonMobil Escorene® LD-336 EVA Film Resin, Clarity, Very High Drawdown (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.5% vinyl acetate copolymer blown film resin capable of very high drawdown with excellent clarity.Applications: Very thin heat seal layers; Light..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO R527-1
Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene LDPE 2004TC37: Light duty film used for very thin films requiring good optical properties for general packaging.Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE, LLDPEContains 1500 ppm slip agent and 2600 ppm antiblocking agentRecommended Applications:General purpose bagVeg..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
SCG Chemicals EL-Leneâ„¢ LD1905FA Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE and LDPE to improve tear resistance and seal strengthContains 1000 ppm slip agent and 700 ppm antiblocking agentR..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 527-3
Borealis Himod™ FT7324 . LDPE for Film Himod FT7324 is a tubular, low-density polyethylene grade for the production of packaging films. Compared to standard LDPE grades, the Himod products provide a combination of higher stiffness and i..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	500 mm/min; ISO 527-3
DuPont Elvaloy® 3217 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3217 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3217 AC has been developed for film applications requiring a combination of softness, toughness and low friction. Typi..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 1184
Carmel Olefins IPETHENE® 320 Low Density Polyethylene IPETHENE® 320 is a general purpose low density polyethylene film extrusion grade, containing no additives. It exhibits good mechanical and optical properties. APPLICATIONS IPETHENE® 320 is mainl..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 1184
Carmel Olefins IPETHENE® 322 Low Density Polyethylene IPETHENE® 322 is a general purpose low density polyethylene film extrusion grade. It contains a medium level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between ..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ISO 1184
Carmel Olefins IPETHENE® 323 Low Density Polyethylene IPETHENE® 323 is a general purpose low density polyethylene film extrusion grade. It contains a high level of anti-blocking and slip additives. It is BHT free. It exhibits a good balance between me..
Film Tensile Strength at Break, TD	>= 15.0 MPa	>= 2180 psi	ASTM D882
Huntsman Rexell® V8402 Cast Film Extrusion LLDPE (discontinued **) Ultra linear-low density copolymer, blown film extrusion, FDA compliant.Features: Excellent mechanical strength, low sealing temperature, and good flex crack resistanceApplications: Sealing layer in..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
Huntsman PE1059 Film Extrusion Polyethylene (discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down and good processability.Applications: Film extrusion: non-abrasive packaging applications.FDA Notes: Conforms to FDA regulation 21 CFR 177..
Film Tensile Strength at Break, TD	15.0 MPa	2180 psi	ASTM D882
Huntsman PE1158 EVA Film Extrusion (discontinued **) 1.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: ..
Film Tensile Strength at Break, TD	15.0 - 18.0 MPa	2180 - 2610 psi	Average value: 17.0 MPa Grade Count:3
Overview of materials for Ethylene Butyl Acrylate This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of approp..