Polymer Property : Film Tensile Strength at Break, TD = 26000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882
DuPont Teijin Films Mylar® M45 Polyester Film, 50 Gauge (15 µm), PVDC Coated  (discontinued **)
Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, dispersion coated on one side with a PVDC copolymer. The coating is an excellent moisture and oxygen barrier. M45..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Melinex® 475 Polyester Film, 200 Gauge
Melinex® 475 is a high yield, translucent polyester film with superb handling properties. Both surfaces are pretreated to promote adhesion to most industrial coatings.General Product Info: This fil..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® EC Polyester Film, 300 Gauge
Mylar® EC films are electrical grade films designed for use in applications where improved dimensional stability is required. In addition to lower levels of shrinkage, Mylar® EC films offer outsta..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® EC Polyester Film, 400 Gauge
Mylar® EC films are electrical grade films designed for use in applications where improved dimensional stability is required. In addition to lower levels of shrinkage, Mylar® EC films offer outsta..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® P25 Polyester Film, 50 Gauge
Product Description: Mylar® P25 is an uncoated, transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. S..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® P25 Polyester Film, 75 Gauge
Product Description: Mylar® P25 is an uncoated, transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. S..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® P25T Polyester Film, 50 Gauge
Product Description: Mylar® P25T is a transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. It has a co..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882A
DuPont Teijin Films Mylar® P25T Polyester Film, 75 Gauge
Product Description: Mylar® P25T is a transparent polyester packaging film designed to be combined with a sealant layer, where the resulting structure will be shallow draw thermoformed. It has a co..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
ASTM D882
DuPont Teijin Films Mylar® M45 Polyester Film, 75 Gauge (22 µm), PVDC Coated  (discontinued **)
Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, dispersion coated on one side with a PVDC copolymer. The coating is an excellent moisture and oxygen barrier. M45..
Film Tensile Strength at Break, TD 179.26 MPa
26000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil
ExxonMobil OPPalyte® 30 HM OPP Film
Product Description: White opaque OPP film with a proprietary cavitated core. Designed for cold seal applications and is used as a surface print, monoweb, or as the inside web of a lamination. Avail..
Film Tensile Strength at Break, TD 179 MPa
26000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 30 HM-3 OPP Film
Product Description: A white opaque OPP film with a proprietary cavitated core. HM-3 is designed for cold seal applications and is used as a surface print, monoweb, or as the inside of lamination. I..
Film Tensile Strength at Break, TD 179 - 248 MPa
26000 - 36000 psi
Average value: 217 MPa Grade Count:10
Overview of materials for Polyvinyl Dichloride (PVDC) Coated Polyester Film
This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Dichloride (PVDC) Coated Polyester Film". Each property range of values reported is minimum an..