Polymer Property : Film Tensile Strength at Break, TD = 5000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
Formosa Plastics Formolene® FORMAX® L91507A Film (Hexene Grade) LLDPE (discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. ..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
Formosa Plastics Formolene® FORMAX® L91507E2 Film (Hexene Grade) LLDPE (discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. ..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE (discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. ..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
M. Holland Company MAGMA® LL1091 LLDPE (discontinued **) Features: Good Heat Seal, Good ToughnessUses: PackagingProcessing Method: ExtrusionInformation provided by M. Holland.
Film Tensile Strength at Break, TD	34.5 - 41.4 MPa	5000 - 6000 psi	ASTM D882
Honeywell ACLAR® 11A (8.00 mil) CTFE Homopolymer, Barrier Film (discontinued **) Description: ACLAR® 11A is a CTFE homopolymer, high performance barrier film for industrial and electronics applications.Information provided by Honeywell.
Film Tensile Strength at Break, TD	34.5 - 41.4 MPa	5000 - 6000 psi	ASTM D882
Honeywell ACLAR® 11A (4.00 mil) CTFE Homopolymer, Barrier Film (discontinued **) Description: ACLAR® 11A is a CTFE homopolymer, high performance barrier film for industrial and electronics applications.Information provided by Honeywell.
Film Tensile Strength at Break, TD	34.5 - 55.2 MPa	5000 - 8000 psi	ASTM D882
Honeywell ACLAR® 22A (2.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide..
Film Tensile Strength at Break, TD	34.5 - 55.2 MPa	5000 - 8000 psi	ASTM D882
Honeywell ACLAR® 22A (1.50 mil) Copolymer Film (discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide..
Film Tensile Strength at Break, TD	34.5 - 48.3 MPa	5000 - 7000 psi	ASTM D882
Honeywell ACLAR® 22C (3.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has moisture barrier and is used for electroluminescent lamps.Information provided by Honeywe..
Film Tensile Strength at Break, TD	34.5 - 48.3 MPa	5000 - 7000 psi	ASTM D882
Honeywell ACLAR® 22C (2.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has moisture barrier and is used for electroluminescent lamps.Information provided by Honeywe..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
LyondellBasell AlathonÂ® L5005 High Density Polyethylene ApplicationsALATHON L 5005 is a high molecular weight high density copolymer that provides broad bimodal molecular weight distribution, high stiffness and good heat seal response and strength. Typi..
Film Tensile Strength at Break, TD	34.5 MPa @Thickness 0.0254 mm	5000 psi @Thickness 0.00100 in	ASTM D882A
Total L425 HDPE Film Blown film polyethylene grade. Provides excellent bubble stability, exceptional tear strength, high impact and puncture resistance, outstanding clarity and gloss, good stiffness, excellent compatibi..
Film Tensile Strength at Break, TD	34.47 MPa	5000 psi	ASTM D882
Formosa Plastics Formolene® L62022B Film (Hexene Grade) LLDPE Hexene Copolymer (Barefoot)Applications: Cast stretch film and high quality packaging films requiring clarity and toughness.A Hexene Copolymer Linear Low Density Polyethylene for film applications i..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin Product Description: LL 3404.48 is a hexane medium density polyethylene cast film grade for applications requiring high strength and high stiffness. Films produced from this resin exhibit good tensi..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi
Dow DOWLEX™ 2036A Linear Low Density Polyethylene, Cast Film Grade DOWLEX® 2036A Polyethylene resin is a cast film polymer having improved thermal stability for high stiffness film applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2a for food ..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
ExxonMobil Escorene™ 768.MJ Blown Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra UL 768.MJ is a low gel 26.2% vinyl acetate copolymer designed for film and compounding applications. This resin provides very low modulus films with high tensile ..
Film Tensile Strength at Break, TD	>= 34.5 MPa	>= 5000 psi	ASTM D 882 A
Total Finathene® HL 328 HDPE resin (discontinued **) Applications: Specialty merchandise bags, millinery/notion bags, mailing envelopes, heavy-duty shipping sacks, shrink films, fresh cut produce packaging, coextrusionInformation provided provided by ..
Film Tensile Strength at Break, TD	34.5 MPa	5000 psi	ASTM D882
M. Holland Company MAGMA® LM115-C LLDPE (discontinued **) Additives: Medium Antiblock, Low SlipFeatures: Good Processability, Good Puncture Resistance, Good Tear Strength, Good ToughnessProcessing Method: ExtrusionInformation provided by M. Holland.