Mechanical Properties Metric English Comments
Flexural Yield Strength 118 MPa
17100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East)
LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE.
Flexural Yield Strength 118 MPa
17100 psi
DIN 53455; ASTM D790
Kolon SPESIN® KP212VO Flame Retardant PBT Resin  (discontinued **)
SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea..
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
Kolon Kocetal® CL704 Reinforced Grade Acetal Copolymer  (discontinued **)
Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ..
Flexural Yield Strength 118 MPa
17100 psi
DIN 53455; ASTM D790
Kolon KOPA® KN131 General Purpose Nylon 6
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Flexural Yield Strength 118 MPa
17100 psi
DIN 53455; ASTM D790
Kolon KOPA® KN333HS Heat Resistant Nylon 66
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin..
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
LG Chemical Lupox® HI2100M PBT+GF10%
Description: Injection Molding, PBT+GF10%, High ImpactApplication: IT/OA, E&E (Bobbin, Switch)CAS No. 65997-17-3, 155123-66-3 and 30965-26-5Information provided by LG Chemical
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
10mm/min; ASTM D790
LG Chemical LUPOY GN1000F PC, Halogen Free, Flame Retardant, Transparency
Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by ..
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
10mm/min; ASTM D790
LG Chemical LUPOY GN1000FA PC, Halogen Free, Flame Retardant, Transparency
Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by ..
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
1.3mm/min; ASTM D790
LG Chemical LUPOY GN2101FC PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance
Description: Injection Molding, PC+GF10%, Halogen Free Flame RetardanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemi..
Flexural Yield Strength 118 MPa

@Temperature 23.0 °C
17100 psi

@Temperature 73.4 °F
ASTM D790
IRPC Polimaxx Polene 120PC Styrene Acrylonitrile
APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN
Flexural Yield Strength 118 MPa

@Temperature 23.0 °C
17100 psi

@Temperature 73.4 °F
ASTM D790
IRPC Polimaxx Polene 121PC Styrene Acrylonitrile
APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN
Flexural Yield Strength 118 MPa

@Temperature 23.0 °C
17100 psi

@Temperature 73.4 °F
ASTM D790
IRPC Polimaxx Polene 129PC Styrene Acrylonitrile
APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP, ELECTRICAL APPLIANCES : ELECTRICAL FAN
Flexural Yield Strength 118 MPa

@Temperature 23.0 °C
17100 psi

@Temperature 73.4 °F
ASTM D790
IRPC Polimaxx Polene 320PC Styrene Acrylonitrile
APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN
Flexural Yield Strength 118 MPa
17100 psi
DIN 53455; ASTM D790
Kolon KOPA® KN133G8ST Multi Reinforced Nylon 6
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Flexural Yield Strength 118 MPa
17100 psi
DIN 53455; ASTM D790
Kolon KOPA® KN133MT40 M/F Reinforced Nylon 6
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr..
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
15mm/min; ASTM D790
LG Chemical 80HFICELLHK SAN, High Transparency, Heat Resistance, Chemical Resistance
Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
17100 psi

@Thickness 0.126 in
10mm/min; ASTM D790
LG Chemical LUPOY GP1000LG PC, Transparent
Description: Injection Molding, PC, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsInformation provided by LG Chemical
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1551GN15 is a reinforced, flame retardant g..
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
Shinkong Synthetic Fibers Shinite® P305G30 PP, 30% Glass Filled
Information from Shinkong Synthetic Fibers Corp.
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific)
Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL LTA5020 PPE+PS
Noryl* LTA5020 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Asia Pacific)
Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e..
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Asia Pacific)
Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can..
Flexural Yield Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Europe-Africa-Middle East)
Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
PlastxWorld CEVIAN® CGF20 20% GF PC/Acrylic Alloy
Glass fiber reinforced PC/Acrylic alloy.These are typical values and are not intended for specification purposes. Information provided by PlastxWorld Inc.
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
PlastxWorld CEVIAN® SKG20 20% GF ABS
Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast..
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
Cheng Yu Plastic N66C2 Nylon 66, 20% Mineral Reinforced
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
Cheng Yu Plastic N6C1 Nylon 6, 10% Mineral Reinforced
Flexural Yield Strength 118 MPa
17100 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL32XXP PC (Europe-Africa-Middle East)
LNP* Lubricomp* DFL32XXP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE.
Flexural Yield Strength 118 MPa
17100 psi
ASTM D790
PlastxWorld CEVIAN®-N 080 SAN resin
These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.