Polymer Property : Flexural Yield Strength = 165 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Yield Strength 165 MPa
23900 psi
ISO 178, ASTM D790
Nilit Nilitop BT G4 FR C3 is a 20% Glass Fiber Reinforced, Flame Retardant PBT
Description: Nilitop BT G4 FR C3 is a 20% glass fiber reinforced, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive. It..
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL14 PC
LNP LUBRICOMP* DFL14 is a compound based on Polycarbonate resin containing 20% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
Flexural Yield Strength 165 MPa

@Strain 3.50 %
23900 psi

@Strain 3.50 %
2 mm/min; ISO 178-A
Lanxess Pocan® ECO T 3215 000000 PBT + PET, 15% Glass Fiber
PBT + PET, 15% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS.
Flexural Yield Strength 165 MPa
24000 psi
Sheet Stress
Hardwire 12x-4-12 Low Density Composite
The 12X Hardwire is a high carbon steel cord with a micro-fine brass or AO-brass (Adhesion Optimized) coating. The 12X wire cord is used where the traits of high tensile strain, excellent conformabi..
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1010A PEI
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1010K PEI (Europe-Africa-Middle East)
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1010KM PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 1010M PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1010RF PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors.This data was supplied by SABIC-IP for the Americas reg..
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1100EF PEI
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1100EF PEI (Europe-Africa-Middle East)
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region..
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 1100F PEI
Standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant. UL94 V0, V2 and 5VA listing. Effective June 2007, this grade will no longer be supported with biocompa..
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 1110F PEI (Asia Pacific)
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact compliant, NSF 51 listing. Effective June 2007, this grade will no longer be supported wit..
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Ultem 1110V PEI (Europe-Africa-Middle East)
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 9011 PEI
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D 790
SABIC Innovative Plastics Ultem MD130A PEI
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength 165 MPa
24000 psi
ASTM D790
Techmer ES Electrafil® J-50/CF/10 Polycarbonate, 10% Carbon Fiber Reinforced
Carbon Fiber Reinforced
Flexural Yield Strength 165 MPa
24000 psi
ASTM D790
Techmer ES HiFill FR® TPX-PBT-00014 40% Glass/Mineral Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 40% Filler by WeightFeatures: Flame RetardantUL File Number: E157318Information provided by TP Composites, Inc.
Flexural Yield Strength 165 MPa
23900 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® SHF4960 PBT
Valox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release.
Flexural Yield Strength 165 MPa
24000 psi
ASTM D790
Techmer ES HiFill® POM CO GF20 UV BK 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforced, 20% Filler by WeightAdditive: UV StabilizerFeatures: Copolymer and Chemically CoupledAppearance: BlackInformati..
Flexural Yield Strength 165 MPa
24000 psi
ASTM D790
Clariant Renol PA143G10 Nylon 6/66 Copolymer, 10% Glass Fiber, Heat Stabilized
Data provided by Clariant Masterbatches
Flexural Yield Strength 165 MPa
23900 psi
ASTM D790
A. Schulman ComAlloy E-13370B Internally Lubricated, Glass Fiber Reinforced Polyester Alloy
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Yield Strength 165 MPa
23900 psi
ASTM D790
PolyOne Edgetek® MP-30GF/000 Modified PPO - 30% Glass Fiber Reinforced  (discontinued **)
Data provided by PolyOne.
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 1000EF PEI (Europe-Africa-Middle East)
Transparent, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS. US FDA and EU Food Contact compliant.
Flexural Yield Strength 165 - 200 MPa
23900 - 29000 psi
Average value: 178 MPa Grade Count:7
Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Recycled, Glass Reinforced". Each property range of values reported is..