- Polymer Property : Flexural Yield Strength = 206 MPa
Polymer Property : Flexural Yield Strength = 206 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM XH2315 TPI Resin Extem XH2315 Resin |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Asia Pacific) Extem XH2315 Resin |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Europe-Africa-Middle East) Extem XH2315 Resin |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN333HB640BL Multi Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | DIN 53455; ASTM D790 |
| Kolon KOPET® KP133G30 FR-PET Resin KOPET® is the FR-PET which realizes the good properties and surface of injection molding with good mold process of short cooling time in low molding temperature.Good mold release, good surface of.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | DIN 53455; ASTM D790 |
| Kolon SPESIN® KP212G30VO G/F Reinforced & Retardant PBT Resin SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP OFL38A PPS - Branched (Europe-Africa-Middle East) LNP* LUBRICOMP* OFL38A is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features include : Internally Lubricated. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2210EPR PEI 20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM AR9200 PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Samyang Tramid® 210G25 Polyamide, Reinforced Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210G25 is a reinforced grade.Applications:Automotive gear level housingConnectors.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® D201G30 PBT, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | Flexural elongation is 2.1%; ASTM D790 |
| Toyobo TS301 PPS, 30% Glass Fiber Reinforced Key Feature: Excellent impact resistance, high flowHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology developed by Toyobo.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Toyobo Vylopet® EMC630 PET/PBT Blend Key Feature: Flame retardant V-0 UL 94 classApplications: general and high rigidity componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, go.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Cheng Yu Plastic A708G3 SAN, 30% Glass Fiber |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Cheng Yu Plastic E2330 Flame Retardant PET, 30% Glass Fiber |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Toyobo Vylopet® EMC120K Glass Reinforced Polyester, Easy Molding Grade Flame retardant V-0 UL-94 classApplications: Electric and electronic componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and trackin.. |
|||
| Flexural Yield Strength | 206 MPa | 29900 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® D201G30 PBT, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||