Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
NYCOA 27/300SR Glass Filled Nylon 6 30% glass filled, flame retardant to UL 94 H-B nylon 6Information provided by NYCOA, Inc. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
NYCOA 27/330KNF Glass Filled Nylon 6 33% glass filled, heat stabilized nylon 6Information provided by NYCOA, Inc. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Dry Nylon 6 - Glass reinforced (43 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP6GF50 Nylon 6, 50% Glass Reinforced, Dry Nylon 6 - Glass reinforced (50 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min; ASTM D790 |
Ovation Polymers RIGITRON 30545 GF Polyester, 45% Glass Reinforced Polyester – 45% Glass Fiber Reinforced PET. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Var.. |
|||
Flexural Yield Strength | 240 - 260 MPa @Temperature 80.0 - 80.0 °C |
34800 - 37700 psi @Temperature 176 - 176 °F |
Average value: 253 MPa Grade Count:4 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-200BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low maintenance mol.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ISO 178 |
Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-220BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications requiring .. |
|||
Flexural Yield Strength | 240 MPa @Thickness 3.20 mm |
34800 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID LW4403B(W) PA66+GF/MF40%, Low Warpage Feature: Injection Molding, PA66+GF/MF40%, Low WarpageApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN135HB40SIBL Multi Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2410EPR PEI 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2410EPR PEI (Asia Pacific) 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM 2410EPR PEI (Europe-Africa-Middle East) 40% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release for enhanced electroplatability. Resin is RoHS compliant. UL94 V0 listing. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF006S is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM HU2410 PEI 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM HU2410 PEI (Asia Pacific) 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem HU2410 PEI (Europe-Africa-Middle East) 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications.
Healthcare management of change, biocompatible (ISO 10993 or USP.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
PlastxWorld Veroplas PB3400 Nylon 66 general purpose, 40% glass filled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
Chem Polymer Chemlon 133 G Nylon 66, 33% Glass Fiber Reinforced A 33% glass fiber reinforced nylon 66 offering excellent high temperature performance, tensile strength and impact resistance.Data provided by the manufacturer, Chem Polymer. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | DIN 53 452 |
Albis Plastics Tedur® P 9519 PPS, ~45% Glass Fiber (black only) Compounded Regrind and/or Production Scrap, Excellent Cost-Performance Ratio. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Handles, Fixing ElementsProcessing: Injec.. |
|||
Flexural Yield Strength | 240 - 400 MPa | 34800 - 58000 psi | Average value: 350 MPa Grade Count:13 |
Overview of materials for Polyvinyl Dichloride (PVDC) This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Dichloride (PVDC)". Each property range of values reported is minimum and maximum values of ap.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM Data |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM Data |
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM Data |
BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G HI HS BK-102 is a 33% glass reinforced, impact modified polyamide 6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in c.. |
|||
Flexural Yield Strength | 240 MPa | 34800 psi | ASTM D790 |
Chevron Phillips Xtel® XK2040 Polyphenylene Sulfide Alloy
(discontinued **) Natural Color Polyphenylene Sulfide AlloyXtel™ XK2040 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength and electrical properties alo.. |