Polymer Property : Flexural Yield Strength = 66.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	66.2 - 297 MPa	9600 - 43100 psi	Average value: 234 MPa Grade Count:23
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler". Specific grades with carbon fiber content bet..
Flexural Yield Strength	66.2 - 278 MPa	9600 - 40300 psi	Average value: 209 MPa Grade Count:57
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini..
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Spartech Royalite R522 PVC Alloy Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech.
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Spartech Royalite R60 PVC/Acrylic Aircraft Grade Sheet Description: Aircraft Grade SheetInformation provided by Spartech.
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Spartech SP-9020 Premium ABS Sheet Description: ABS SheetInformation provided by Spartech.
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Techmer ES PlaslubeÂ® AC-80/TF/15 Acetal (Copolymer), 15% PTFE Plaslube polytetrafluoroethylene (PTFE) lubricated acetal copolymer grades offer additional wear and friction performance over neat acetal. Typical applications include bearings, slides and small g..
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Clariant PA131 Nylon 66, Highly Impact Modified Data provided by Clariant Masterbatches
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Clariant PA131G2GN-91 Green Nylon 66, Highly Toughened Data provided by Clariant Masterbatches
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Clariant Renol PA133 Nylon 66, Highly Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches
Flexural Yield Strength	66.2 MPa	9600 psi	ASTM D790
Clariant Renol PA133GN-109 Nylon 66, High Impact, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron HR-60 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Abstron HR60N ABS Heat Resistant High ImpactInformation provided by Bhansali
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron HR-60 ABS Heat Resistant High, Medium Impact Heat Resistant Grades with good flowInformation provided by Bhansali
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	ASTM D-790
Bhansali Engineering Abstron IM-11G ABS Injection Molding Grade High Impact, High Rigidity, High Fatigue, Low Flow, PaintableInformation provided by Bhansali
Flexural Yield Strength	66.2 MPa @Thickness 6.40 mm	9600 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Abstron HR60N ABS Heat Resistant High ImpactInformation provided by Bhansali