Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® FXC810AL PC+ABS (Europe-Africa-Middle East) CYCOLOY FXC810AL is a multi-purpose PC+ABS injection moulding grade, suitable for those applications that require Alpine White colour effects. The colour package may effect performance.This data was.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS (Europe-Africa-Middle East) PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat AgingThis data was supplied by SABIC-IP for the Eur.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 905AU PC (Asia Pacific) LEXAN resin grade 905AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in all colors, intended to .. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Ineos Nova 2110 General Purpose Crystal Polystyrene
(discontinued **) Moderately high heat resistance, Good balance of strength and ease of processing, USP Class VIApplications: Foam extrusion, Biaxially oriented sheet, Thermoformed drinkware, Molded packagingExposure.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® BFL4000U PC Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Global PC/ABS QX-7004 Molding Grade PC/ABS
(discontinued **) Information provided by Global Polymers Corporation. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
PolyOne Lubri-Tech™ AT-000/08T Acetal - 8% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Plenco 204 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound
(discontinued **) Plaslok 204 is a two-stage, woodflour and mineral-filled phenolic molding compound formulated to accommodate a wide range of molding situations. In addition, it is recommended for use in thin wall .. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Plenco 308 Black (COM) Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 308 is a two-stage, mineral and flock-filled phenolic molding compound designed to withstand the hostile environment of high abrasion and high tangential speed of engine pulleys. It is char.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
Plenco 309 Black (COM) Mineral/Fiber Filled Phenolic Molding Compound
(discontinued **) Plaslok 309 is a two-stage, mineral and fiber-filled phenolic molding compound having excellent impact strength; and as such, is considered a good candidate for replacing chopped-fiber filled compou.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
LG Chemical LI-921 ASA, Extrusion, High Stiffness Information Provided by LG Chem |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC LNP* Lubricomp* Lexan_WR5210R compound is a wear resistant, 7% PTFE filled PC. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RL0039XP PA 66 (Europe-Africa-Middle East) LNP* LUBRICOMP* RL0039XP is a compound based on PA66 resin containing PTFE, Flame Retardant. Added features include ; Flame Retardant, internally Lubricated. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Asia Pacific) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF741XXH PP LNP* THERMOCOMP* MF741XXH is a compound based on Polypropylene reain containing Glass Fiber and proprietay antimicrobial additives. Designed for touch surfaces in patient critical healthcare applic.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PVX0800 PPE NORYL* PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2205 Polycarbonate, Injection Grade Exceptionally good flow injection molding grade with easy mold release, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialSc.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2405 Polycarbonate, Injection Grade Very easy flowing injection molding grade with easy mold release, Makrolon grade 2458 for food contact applications.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was se.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 2458 Polycarbonate, Injection Grade Very easy flowing BgVV- and FDA injection molding grade with easy mold release, for food contact applications, better resistance to hot water.Information provided by Bayer.As of 1 September 2015, Ba.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® 6255 Polycarbonate, Flame Retardant, High Productivity, Mold Release Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | at 5% strain; ASTM D790 |
Covestro Makrolon® T 7435 Polycarbonate, High Impact Impact modified injection molding grade, extremely easy flow and easy mold release, housings for portable mobile phones.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience wa.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboWeld 48-8/AboCure 48-8 Adhesive/Casting Resin Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Flexural Yield Strength | 83.0 MPa | 12000 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 37-10/AboCure 37-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Flexural Yield Strength | 83.0 - 207 MPa | 12000 - 30000 psi | Average value: 158 MPa Grade Count:21 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is .. |