Polymer Property : Tensile Strength, Ultimate = 114000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 785 MPa

@Temperature 600.0 °C
 114000 psi

@Temperature 1112 °F
International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel
Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki..
Tensile Strength, Ultimate 788 MPa

@Thickness 12.7 mm,
Temperature 93.0 °C
 114000 psi

@Thickness 0.500 in,
Temperature 199 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 789 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 204 °C
 114000 psi

@Thickness 0.374 - 1.00 in,
Temperature 399 °F
Haynes Hastelloy® S alloy, flat products
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate 786 MPa

@Thickness 12.7 mm,
Temperature 538 °C
 114000 psi

@Thickness 0.500 in,
Temperature 1000 °F
Haynes Ultimet® alloy, plate, GMAW weld (short)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate 787 MPa

@Temperature 650 °C
 114000 psi

@Temperature 1200 °F
 AMS 5879
Haynes 625SQ® Nickel Alloy Sheet
Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200°F (649Â..
Tensile Strength, Ultimate 783 MPa

@Thickness 12.7 mm,
Temperature 25.0 °C
 114000 psi

@Thickness 0.500 in,
Temperature 77.0 °F
Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate 786 MPa

@Thickness 12.7 mm,
Temperature 20.0 °C
 114000 psi

@Thickness 0.500 in,
Temperature 68.0 °F
Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate
HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate 789 MPa

@Thickness 12.7 mm,
Temperature 93.0 °C
 114000 psi

@Thickness 0.500 in,
Temperature 199 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 789 MPa

@Thickness 3.20 mm,
Temperature 149 °C
 114000 psi

@Thickness 0.126 in,
Temperature 300 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 783 MPa

@Temperature 23.0 °C
 114000 psi

@Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Type 201, 5% Cold Work (UNS S20100)
Allegheny Ludlum Type 201 and 201L have the greatest tonnage of the Cr-Ni-Mn steels (200 series). Type 201 provides advantages over the 18-8 grades in certain applications. Lower cost manganese an..
Tensile Strength, Ultimate 785 MPa

@Thickness 12.7 mm,
Temperature 25.0 °C
 114000 psi

@Thickness 0.500 in,
Temperature 77.0 °F
 as welded
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately doubl..
Tensile Strength, Ultimate 783 MPa

@Thickness 4.00 mm,
Temperature 20.0 °C
 114000 psi

@Thickness 0.157 in,
Temperature 68.0 °F
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate 786 MPa

@Temperature 149 °C
 114000 psi

@Temperature 300 °F
 Cold Worked
ATI Wah Chang TI-3Al-2.5V
Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an..