Polymer Property : Tensile Strength, Ultimate = 779 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	779 MPa @Thickness 12.7 mm, Temperature 538 Â°C	113000 psi @Thickness 0.500 in, Temperature 1000 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	779 MPa @Thickness 19.0 mm, Temperature 538 Â°C	113000 psi @Thickness 0.750 in, Temperature 1000 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate	779 MPa @Thickness 6.35 mm	113000 psi @Thickness 0.250 in
Haynes HastelloyÂ® C-2000Â® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h..
Tensile Strength, Ultimate	779 MPa @Temperature 538 °C	113000 psi @Temperature 1000 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	779 MPa @Temperature 538 °C	113000 psi @Temperature 1000 °F
Astaras ANVILOY® 1150 Tungsten Based High Temp Alloy Anviloy® 1150 is a tungsten-based material that was developed primarily for die-casting, aluminum permanent mold, and difficult extrusions. It is produced by a high temperature powder metallurgy pr..
Tensile Strength, Ultimate	779 MPa @Temperature 25.0 °C	113000 psi @Temperature 77.0 °F
Haynes 617 Nickel Alloy Plate Haynes 617 alloy is a nickel-chromium-cobalt-molybdenum alloy with a good combination of metallurgical stability, strength, and oxidation resistance at high temperatures. The alloy is readily formed..