Polymer Property : Tensile Modulus = 377 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Crastin® S600F20 NC010 PBT  (Unverified Data**)
Crastin® S600F20 NC010 is an unreinforced, lubricated, medium viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Modulus 2.60 GPa

@Temperature -18.0 °C
377 ksi

@Temperature -0.400 °F
ASTM-D638
Ineos ABS Lustran® LK197 ABS, Extrusion Grade
Lustran® ABS LK197 resin is a high-gloss, medium-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). It provides a superior balance between rigidity and impact strength, as well as e..
Tensile Modulus 2.60 GPa

@Temperature 150 °C
377 ksi

@Temperature 302 °F
LATI Latamid 12 H2 K/30 PA 12, 30% Carbon Fiber Reinforced, Heat Stabilized
Polyamide 12 (PA12) based compound. Heat stabilized. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termop..
Tensile Modulus 2.60 GPa

@Temperature 120 °C
377 ksi

@Temperature 248 °F
LATI Kelon® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized
Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Low thermal expansion coefficient. Very high dimensional stab..
Tensile Modulus 2.60 GPa

@Temperature 150 °C
377 ksi

@Temperature 302 °F
LATI Kelon® B FR H CETG/250-V0 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacifi..
Tensile Modulus 2.60 GPa

@Temperature 150 °C
377 ksi

@Temperature 302 °F
LATI Lapex A PES
Polyether Sulfone (PES). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInf..
Tensile Modulus 2.60 GPa

@Temperature 90.0 °C
377 ksi

@Temperature 194 °F
LATI Lapex R PPSU
Polyphenylene Sulfone (PPSU). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ameri..
Tensile Modulus 2.60 GPa

@Temperature 90.0 °C
377 ksi

@Temperature 194 °F
LATI Latamid 6 H2 G/20-V2HF PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Middle East; Asia Pacific; Euro..
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
LATI Latan 2 POM
Polyoxymethylene (POM). Unfilled. High viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati..
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
LATI Latan 9 POM
Polyoxymethylene (POM). Unfilled. Medium viscosity. Very good tribological properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La..
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Special mineral filler. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North A..
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
LATI Latene® EP 7 TES/30 PP Copolymer, 30% Talc filled
Polypropylene copolymer (PPc) based compound. Aesthetic talc. Very good surface appearance. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInfo..
Tensile Modulus 2.60 GPa

@Temperature 150 °C
377 ksi

@Temperature 302 °F
LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced
Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast..
Tensile Modulus 2.60 GPa

@Temperature 23.0 °C
377 ksi

@Temperature 73.4 °F
LATI Latigray 53/22-01 CX/25 PP Homopolymer, Impact Modified
Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformatio..
Tensile Modulus 2.60 GPa

@Thickness 1.50 mm,
Temperature 90.0 °C
377 ksi

@Thickness 0.0591 in,
Temperature 194 °F
BASF Ultraform N 2320 003 UNC Q600 POM
Ultraform N 2320 003 UNC Q600 is a rapidly solidifying grade of POM for injection molding. Contains a mold release agent.
Tensile Modulus 2.60 GPa

@Temperature 150 °C
377 ksi

@Temperature 302 °F
LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati..