Polymer Property : Compressive Strength = 34.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	34.3 MPa @Temperature 1100 Â°C	4980 psi @Temperature 2010 Â°F	Cold Crushing
Sharadaa Ceramics REFCAST K SUPER High Alumina Castables Description: We bring to our clients a qualitative range of Dense Alumina Castables that are conventional castable of medium purity. These castables cater to the application needs of various industr..
Compressive Strength	34.3 MPa @Temperature 110 Â°C	4980 psi @Temperature 230 Â°F	Cold Crushing
Sharadaa Ceramics REFCAST NORMAL Dense Castables Description: We offer a range of Dense Castables that are conventional castable and extensively used in boiler work, general furnace and burner blocks. Made as per international standards, our range..
Compressive Strength	>= 34.3 MPa @Temperature 1100 Â°C, Time 10800 sec	>= 4980 psi @Temperature 2010 Â°F, Time 3.00 hour	Cold Crushing, Specification, After firing @ 1100Â°C
Sharadaa Ceramics REFPLAST 60 60% Alumina Plastic Nature of bond: Chemical-CeramicInstallation: Pneumatic rammingInformation provided by Sharadaa Ceramics Pvt. Ltd.
Compressive Strength	34.3 MPa @Temperature 800 Â°C	4980 psi @Temperature 1470 Â°F	Cold Crushing
Sharadaa Ceramics Sharada RFC-45 Gel Bonded Castables Mullite Bonded Free Flowing Cement Free Versatile Castable SystemProduct Characteristics: High Mullitisation, Free from Low Temperature eutectics, Non wetting to molten metals Ferrous/Non Ferrous, E..
Compressive Strength	34.3 MPa @Temperature 800 Â°C	4980 psi @Temperature 1470 Â°F	Cold Crushing
Sharadaa Ceramics Sharada RFC-Fused Silica Gel Bonded Castables Mullite Bonded Free Flowing Cement Free Versatile Castable SystemProduct Characteristics: High Mullitisation, Free from Low Temperature eutectics, Non wetting to molten metals Ferrous/Non Ferrous, E..
Compressive Strength	34.3 MPa @Time 86400 sec	4980 psi @Time 24.0 hour	Cold Crushing
Sharadaa Ceramics THERMO PATCH EXCEL High Alumina Castables Description: We bring to our clients a qualitative range of Dense Alumina Castables that are conventional castable of medium purity. These castables cater to the application needs of various industr..
Compressive Strength	34.3 MPa @Temperature 110 Â°C	4980 psi @Temperature 230 Â°F	Cold Crushing
Sharadaa Ceramics ZAP 001 Smart Cast Application Special Properties: Thermal Shock Slag ResistanceIndustry: FoundryApplication Areas: Foundry LaddleInformation provided by Sharadaa Ceramics Pvt. Ltd.
Compressive Strength	34.3 MPa @Temperature 110 Â°C	4980 psi @Temperature 230 Â°F	Cold Crushing
Sharadaa Ceramics ZAP 006 Smart Cast Application Special Properties: Thermal Shock, Flame ErosionIndustry: Multi PurposeApplication: Burner Blocks all types of Thermal Shock ApplicationsInformation provided by Sharadaa Ceramics Pvt. Ltd.
Compressive Strength	34.3 MPa @Temperature 110 Â°C	4980 psi @Temperature 230 Â°F	Cold Crushing
Sharadaa Ceramics ZAP 008 Smart Cast Application Special Properties: Thermal Shock Slag ResistanceIndustry: SteelApplication: Pig Iron Laddle Safety Layer, Sponge Iron Rotary Kiln BackupInformation provided by Sharadaa Ceramics Pvt. Ltd.
Compressive Strength	34.3 MPa @Strain 1.00 %	4970 psi @Strain 1.00 %	ASTM D695
Daelim H&L Plavis-G40 ISO 40% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 car..
Compressive Strength	34.3 MPa @Strain 1.00 %	4970 psi @Strain 1.00 %	ASTM D695
Daelim H&L Plavis-MS CM MoS2 Filled Aromatic Polyimide Bearing Compression Molded. Plavis-MS: MoS2 15 wt% filled, Self lubricating grade for vacuum environments.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is the ..
Compressive Strength	34.3 MPa @Strain 1.00 %	4970 psi @Strain 1.00 %	ASTM D695
Daelim H&L Plavis-MS DF MoS2 Filled Aromatic Polyimide Bearing Direct Formed. Plavis-MS: MoS2 15 wt% filled, Self lubricating grade for vacuum environments.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is the criti..
Compressive Strength	34.3 MPa @Temperature 1000 °C, Time 10800 sec	4980 psi @Temperature 1830 °F, Time 3.00 hour	Cold Crushing Strength
Chosun Refractories APC-120 Acid-proof Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 1500 °C, Time 10800 sec	4980 psi @Temperature 2730 °F, Time 3.00 hour	Cold Crushing Strength
Chosun Refractories CTL-Z1 Monolithic Refractories for Ladle and Tundish Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 - 39.2 MPa @Temperature 1350 °C, Time 10800 sec	4980 - 5690 psi @Temperature 2460 °F, Time 3.00 hour	Cold Crushing Strength
Chosun Refractories HACT-180 High Alumina Castables Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 - 39.2 MPa @Temperature 110 °C, Time 86400 sec	4980 - 5690 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories HACT-180 High Alumina Castables Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 - 44.1 MPa @Temperature 1350 °C, Time 10800 sec	4980 - 6400 psi @Temperature 2460 °F, Time 3.00 hour	Cold Crushing Strength
Chosun Refractories HACT-180G High Alumina Castables Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 1350 °C, Time 10800 sec	4980 psi @Temperature 2460 °F, Time 3.00 hour	Cold Crushing Strength
Chosun Refractories HSC-15G Dense and High-Strength Castable, Credens Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories IJM-1 Special Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories joint-1 Blast Furnace Runner Refractory Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories LPCT-18PI Lance Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories MMCT-75 Special Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories SCX-85 I Special SiC Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories TCH-175S Torpedo Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
Compressive Strength	34.3 MPa @Temperature 110 °C, Time 86400 sec	4980 psi @Temperature 230 °F, Time 24.0 hour	Cold Crushing Strength
Chosun Refractories TCH-175Y Torpedo Castable Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).