Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Peel Strength | 2.98 kN/m @Temperature 21.1 °C |
17.0 pli @Temperature 70.0 °F |
T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876 |
Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive Aroply™ 350 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported carrier. Cured adhesive character.. |
|||
Peel Strength | 2.98 kN/m @Temperature 21.1 °C |
17.0 pli @Temperature 70.0 °F |
Bell Peel |
Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components Redux 609 is a 250°F curing modified epoxy film adhesive containing a cottom scrim for easy handling and glue-line thickness control. It is available at standard areal weights of 0.06 psf and 0.04 .. |
|||
Peel Strength | 2.98 kN/m @Time 259000 sec |
17.0 pli @Time 72.0 hour |
Adhesion to Truck Paint; ASTM D3330 |
3M 4412G Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough .. |
|||
Peel Strength | 2.98 kN/m @Time 259000 sec |
17.0 pli @Time 72.0 hour |
Adhesion to Acrylic; ASTM D3330 |
3M 4412G Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough .. |
|||
Peel Strength | 2.98 kN/m @Time 259000 sec |
17.0 pli @Time 72.0 hour |
Adhesion to PP; ASTM D3330 |
3M 4412G Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough .. |
|||
Peel Strength | 2.98 kN/m @Temperature 24.0 °C, Time 432000 sec |
17.0 pli @Temperature 75.2 °F, Time 120 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 10 Neoprene Contact Adhesive 3M™ Scotch-Weld™ Neoprene Contact Adhesive 10 is a multi-purpose contact adhesive which may be used to bond plastic laminate, aluminum, steel, wallboard, wood, masonry, rubber and canvas.Informati.. |
|||
Peel Strength | 2.98 kN/m @Temperature 23.0 °C |
17.0 pli @Temperature 73.4 °F |
180° T-Peel, Red SBR/CRS |
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Peel Strength | 2.98 kN/m @Time 259000 sec |
17.0 pli @Time 72.0 hour |
Adhesion to Stainless; ASTM D3330 |
3M 4411B Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough .. |
|||
Peel Strength | 2.98 kN/m @Time 259000 sec |
17.0 pli @Time 72.0 hour |
Adhesion to Truck Paint; ASTM D3330 |
3M 4411B Extreme Sealing Tape 3M™ Extreme Sealing Tape is a family of single coated, pressure sensitive adhesive tapes designed for difficult sealing applications. The backing on this tape is an ionomer film that is very tough .. |
|||
Peel Strength | 2.98 kN/m @Temperature 66.0 °C, Time 1.81e+6 sec |
17.0 pli @Temperature 151 °F, Time 504 hour |
180°, Canvas/Steel |
3M Scotch-Weld™ 4475 Industrial Adhesive Features: Dries quickly to a firm bondExcellent resistance to water, plasticizer migration, many detergent and soap solutions, oils and greasesA general purpose adhesive for bonding most vinyls, cer.. |
|||
Peel Strength | 2.98 kN/m @Temperature 24.0 °C |
17.0 pli @Temperature 75.2 °F |
180°, Canvas/Steel |
3M Scotch-Weld™ 826 Nitrile Rubber & Plastic Adhesive Features: A light colored, fast drying adhesiveExcellent resistance to aromatic fuels, water and oilUsed to bond many types of plastic films including ABS, cellulose acetate, and PVCInformation prov.. |