Polymer Property : Fatigue Strength = 280 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Fatigue Strength	280 MPa @Strain 0.200 %	40600 psi @Strain 0.200 %	R=smin/smax=0.1; 2 million cycles, F50
Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 174 Strip; 1/2HT (TH02) Temper (UNS C17410) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 95%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 174 Strip; HT (TH04) Temper (UNS C17410) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 95%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	280 - 320 MPa @# of Cycles 1.00e+8	40600 - 46400 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 190 Strip; 1/4HM (TM01) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 190 Strip; AM (TM00) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 25 Strip; AT (TF00) Temper (UNS C17200) Treatment required for max strength: 3 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 96%Stress Relaxation after 1000 hrs @ 200Â°C: 70%Superficial Hardness: 30N 56-6..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM00 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Fatigue Strength	280 - 310 MPa @# of Cycles 1.00e+8	40600 - 45000 psi @# of Cycles 1.00e+8	Reverse Bending (R=1)
Materion Beryllium Copper Alloy 25 Strip; 1/4HT (TH01) Temper (UNS C17200) Treatment required for max strength: 2 hrs @ 315ÂºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 96%Stress Relaxation after 1000 hrs @ 200Â°C: 70%Superficial Hardness: 30N 56-6..
Fatigue Strength	280 MPa	40600 psi	test conditions not reported
ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 760°C (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties..