Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | X, Y direction; ASTM D638 |
Rogers Corporation RT/duroid® 6002 High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Trefsin® 3201-75 W305 Thermoplastic Rubber
(discontinued **) A natural thermoplastic elastomer with excellent permeation resistance to water, air and other gases. It can be processed using injection molding, extrusion, blow molding or other melt processing t.. |
|||
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 5501 LC GREY Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | molded-without post cure; ASTM D412 |
Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | molded-without post cure; ASTM D412 |
Multibase C6-235 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 8980-60 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 8999-65 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 9980-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 9999-65 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | Dry; ASTM D412 |
Lubrizol Estane® ALR G500 Water Absorbent Thermoplastic Polyurethane Type: Estane® ALR G500 is an aliphatic thermoplastic polyurethane (TPU) resin designed to absorb water and transport moisture.Features: Contains UV additivesAvailable in AmericasInformation Provide.. |
|||
Tensile Strength, Ultimate | 6.90 MPa @Temperature 49.0 °C |
1000 psi @Temperature 120 °F |
Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dow Corning SILASTIC® 37084-D SILICONE RUBBER BLACK 40 Durometer, peroxide cured, low compression set Silicone Rubber CompoundInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dow Corning SILASTIC® S RTV SILICONE RUBBER BASE & GREEN CURING AGENT High strength silicone rubber suited for prototyping, production tooling, artistic and renovation applications. Silastic S is recommended for use with polyesters, cement and rigid polyurethanes; als.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Cytec EN-2527 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8200 Polyolefin Elastomer Description: Engage® 8200 and Engage® 8207 polyolefin elastomers are ethylene-octene copolymers that have excellent flow characteristics and performs well in a wide range of general purpose thermo.. |
|||
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8207 Polyolefin Elastomer Description: Engage® 8207 polyolefin elastomer is a loose talc surface coated ethylene-octene copolymer. The talc is untreated and has a nominal 1µm particle size. This product offers the exceptio.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dymax 9-20558 Conformal Coating High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9-20558 Conformal CoatingThick barrier coating; excellent protection of sensitive circuits from moisture. Cure Speed.. |
|||
Tensile Strength, Ultimate | >= 6.90 MPa | >= 1000 psi | |
Arlon 0.015" (0.381 mm) Layer-on-Layer Silicone Traction Motor Insulation (51229R015) 0.005 in. (0.1 mm) minimum uncured silicone on 0.002 in. (0.5 mm) minimum cured silicone on 0.008 in. (0.2 mm) nominal Prime Coated 7628 Fiberglass; 0.003 in. (0.08 mm) polyethylene interleave; over.. |
|||
Tensile Strength, Ultimate | >= 6.90 MPa | >= 1000 psi | |
Arlon 0.030" (0.762 mm) Silicone Traction Motor Insulation with Fiberglass Substrate (19220R030) Uncured silicone rubber with a minimum thickness of 0.015 in.(0.38 mm) on Prime Coated 1523 Fiberglass; 0.0015 in. (0.8 mm) polyethylene interleave; overall thickness 0.030 in ± 0.003 (0.76 mm ± 0.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
Arlon 25188T017 Silicone Rubber/Laminated ETFE Film Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate Low outgassing, thermally conductive, electrically insulating, Thermabond®. Bonds with primer. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass. |
|||
Tensile Strength, Ultimate | >= 6.90 MPa | >= 1000 psi | |
Arlon Thermavac® 0.030" (0.762 mm) Uncured Silicone Vacuum Bagging (30400N030) Uncured, unsupported silicone rubber with a thickness of 0.030 in ± 0.003 (0.76 mm ± 0.038) on a Kodacel carrier (0.005 in., 0.13 mm nominal thickness); 0.003 in. (0.8 mm) polyethylene interleave... |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | ASTM D412; ISO 37 |
Advanced Polymer Alloys Alcryn® 2250 UT Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 6.90 MPa | 1000 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Santoprene® 281-64 Thermoplastic Rubber
(discontinued **) A colorable thermoplastic medical grade elastomer with good fluid resistance, certified non-toxic by MEM elution test. It has USP Class VI Certificate of Compliance for biocompatibility and can be .. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | ASTM D412 |
Arlon R3781-920-##R##-P0 Silicone Rubber This fusible silicone tape is specially formulated to yield improved flexibility, elongation and elastic recovery at low operating temperature (-70°C to -100°C) where standard fusible silicone tap.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | TM R050-36 |
Resinlab® EP1200LV Casting Resin Resinlab™ EP1200LV a low viscosity version of EP1200, a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity, flexibility an.. |
|||
Tensile Strength, Ultimate | 6.89 - 24.1 MPa | 1000 - 3500 psi | Reinforced |
Nitrile Rubber (NBR, Acrylonitrile-Butadiene Rubber) Nitrile Rubbers are copolymers of butadiene and acrylonitrile. The term has also been applied to copolymers of other dienes and/or nitriles. Acrylonitrile content may range from 18-50%. Increasin.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Loctite® 5145 Form-In-Place Adhesive/Sealant Gasketing and Wire TackersLoctite® innovative gasketing products offer precise, reliable sealing of electronic enclosures, protecting them from environmental hazards. Loctite offers both Form-in-pl.. |
|||
Tensile Strength, Ultimate | 6.89 - 130 MPa | 1000 - 18900 psi | Average value: 80.8 MPa Grade Count:184 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |