Polymer Property : Tensile Strength, Ultimate = 1020 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 7.03 MPa
1020 psi
ASTM D638
Global ST-1018 Low Density Polyethylene, Injection Molding Grade  (discontinued **)
Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-packagingMeets FDA requirements as listed in food additives regulation 21 CFR 117.15..
Tensile Strength, Ultimate 7.03 MPa
1020 psi
ASTM D638
Global SU-1018 Low Density Polyethylene, Injection Molding Grade  (discontinued **)
Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-packagingMeets FDA requirements as listed in food additives regulation 21 CFR 117.15..
Tensile Strength, Ultimate 7.00 - 23.0 MPa
1020 - 3340 psi
Average value: 10.5 MPa Grade Count:8
Overview of materials for Polytetrafluoroethylene (PTFE), Mica Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Mica Filled". Each property range of values reported is minimum and maxi..
Tensile Strength, Ultimate 7.00 - 17.0 MPa

@Temperature 250 - 250 °C
1020 - 2470 psi

@Temperature 482 - 482 °F
Average value: 11.0 MPa Grade Count:8
Overview of materials for Polyperfluoroalkoxyethylene (PFA), Molded/Extruded
This property data is a summary of similar materials in the MatWeb database for the category "Polyperfluoroalkoxyethylene, Molded/Extruded". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate 7.00 MPa
1020 psi
Original Properties; ASTM D412 Die C
Freudenberg Simrit S40 Silicone Elastomer (VMQ)
General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasol..
Tensile Strength, Ultimate 7.06 MPa

@Treatment Temp. 150 °C,
Time 605000 sec
1020 psi

@Treatment Temp. 302 °F,
Time 168 hour
Heat Aging; ASTM D 412/ASTM D 573
Zylog Neoplast® 173 C Thermoplastic Vulcanizate
Neoplast 173 C is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding and Extrusion applications.RoHS Compliant, UV S..
Tensile Strength, Ultimate 7.00 MPa
1020 psi
Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4770P Highly Extended Low-Cost Hose
FormulationNordel® IP 4770P
Tensile Strength, Ultimate 7.00 MPa
1020 psi
Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4770R Highly Extended Low-Cost Hose
FormulationNordel® IP 4770R
Tensile Strength, Ultimate 7.00 - 18.0 MPa
1020 - 2610 psi
ATG s.r.l. BR Polybutadiene Rubber
Tensile Strength, Ultimate 7.00 - 24.0 MPa
1020 - 3480 psi
ATG s.r.l. CR Polychloroprene
Tensile Strength, Ultimate 7.00 - 18.0 MPa
1020 - 2610 psi
ATG s.r.l. IIR Butyl Rubber
Tensile Strength, Ultimate 7.00 - 25.0 MPa
1020 - 3630 psi
ATG s.r.l. NBR Nitrile-Butadiene Rubber
Tensile Strength, Ultimate 7.00 - 28.0 MPa
1020 - 4060 psi
ATG s.r.l. SBR Styrene-Butadiene Rubber
Tensile Strength, Ultimate 7.00 MPa

@Temperature 250 °C
1020 psi

@Temperature 482 °F
ASTM D638
Asahi Glass Fluon® P-62XP PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Tensile Strength, Ultimate 7.00 MPa

@Temperature 250 °C
1020 psi

@Temperature 482 °F
ASTM D638
Asahi Glass Fluon® P-830UP PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Tensile Strength, Ultimate 7.00 MPa
1020 psi
ASTM D638
Toyobo Pelprene™ P-30B Polyester TPE
Key Feature: Pelprene P typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'P' type is a block..
Tensile Strength, Ultimate 7.00 - 57.0 MPa
1020 - 8270 psi
Average value: 27.1 MPa Grade Count:69
Overview of materials for Polyether Ester Elastomer
This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr..
Tensile Strength, Ultimate 7.00 - 45.0 MPa

@Temperature 60.0 - 90.0 °C
1020 - 6530 psi

@Temperature 140 - 194 °F
Average value: 16.9 MPa Grade Count:4
Overview of materials for Polypropylene, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Flame Retardant". Each property range of values reported is minimum and maximum values of..
Tensile Strength, Ultimate 7.00 - 18.0 MPa

@Temperature 60.0 - 120 °C
1020 - 2610 psi

@Temperature 140 - 248 °F
Average value: 12.3 MPa Grade Count:1
Overview of materials for Polypropylene with 40% Talc Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are..
Tensile Strength, Ultimate 7.00 - 16.0 MPa

@Temperature 60.0 - 120 °C
1020 - 2320 psi

@Temperature 140 - 248 °F
Average value: 11.4 MPa Grade Count:4
Overview of materials for Polypropylene, Mineral Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values..