Polymer Property : Tensile Strength, Ultimate = 1080 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1080 MPa	157000 psi
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	1080 MPa @Temperature 540 Â°C	157000 psi @Temperature 1000 Â°F
Haynes 242Â® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Ultimate	1080 MPa	157000 psi	Typical
TIMET TIMETAL® 550 (Ti-4Al-4Mo-2Sn) Titanium Alloy Solution Treated High-Strength Forging AlloyIndustry Specifications: Germany Aerospace: 3.7184. France: T-A4DE. UK Aerospace Specifications BS TA. 45, 46, 47, 48,49, 50, 51, 57.Features: TIMETAL 550, like TIMETAL..
Tensile Strength, Ultimate	1080 MPa @Diameter 25.4 mm	156000 psi @Diameter 1.00 in	R<sub>m</sub>. Bar. 310 HB
Assab Steels 618 Plastic Mold Material ASSAB 618 is a vacuum-degassed Cr-Ni-Mo-alloy steel which is supplied in the hardened and tempered condition. ASSAB 618 is manufactured to consistently high quality standards with a controlled sulfu..
Tensile Strength, Ultimate	1080 MPa @Diameter 25.4 mm	156000 psi @Diameter 1.00 in	R<sub>m</sub>. Bar. 310 HB
Assab Steels 718HH Plastic Mold Material IMPAX SUPREME is a premium-quality vacuum-degassed Cr-Ni-Mo-alloyed steel which is supplied in the hardened and tempered condition. IMPAX SUPREME is manufactured to consistently high quality standar..
Tensile Strength, Ultimate	1080 MPa	157000 psi
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..