Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Lubri-Tech™ PK-15GP/5T Polyetheretherketone (PEEK), PTFE Lubricated
(discontinued **) Description/Features:Graphite LubricatedPTFE LubricatedInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
ExxonMobil Escor® AT-320 EMAAA Terpolymer for Polymer Modification
(discontinued **) Data provided by the manufacturer, Exxon Chemical.45 Acid Number. Provides unusual adhesion to a variety of substrates and other components, such as aluminum foil, polyolefins, polycarbonate, PET, .. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D882 |
SABIC Innovative Plastics Lexan® FR735A Polycarbonate Film, Flame Retardant Lexan FR735A is a black, one side velvet, one polish flame-retardant polycarbonate film with a UL94 V-0 listing at 0.250 mm. This film has formability, excellent mechanical properties, good dimensio.. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® AS-40GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 76.0 - 175 MPa | 11000 - 25400 psi | Average value: 132 MPa Grade Count:24 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D638 |
Technetics Group Amicon™ Nylon 6/66
(Unverified Data**) Information provided by Technetics Group (formerly Plastomer Technologies) |
|||
Tensile Strength, Ultimate | 75.5 MPa | 11000 psi | ASTM D638 |
Samsung Cheil Industries Starex® HF-5330S ASA, Unreinforced
(discontinued **) Amorphous Styrene Acrylonitrile (SAN)Characteristics: Heat Resistant: Impact and Chemical Resistance, Surface GlossApplications: Oil Filter Case, Lubricant Can, Refrigerator and Hair Dryer Component.. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D882 |
Honeywell Capran® 996 Heat Stabilized Nylon Film
(discontinued **) Description: Capran® 996 is a blue tinted, heat-stabilized cast film produced from modified nylon resin. Capran® 996 has excellent heat stability and resistance to pinholing. It can be used at t.. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | |
Haysite H755 Glass Reinforced Polyester Sheet, Electrical Grade (GPO1) A new generation of IEEE Class F, 155ºC /165ºC NEMA GPO- 1 material. H755 is designed to bridge the gap between 130ºC Class B GPO-1 materials and Class H 180ºC grades. H755 has quickly g.. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | |
Haysite Ultratrac® H950 Glass Reinforced Polyester Sheet, Electrical Grade (GPO3) This new generation of high performance material meets or exceeds all requirements for NEMA GPO-2 or GPO-3. ULTRATRAC ® H950 is recognized by U.L. as a 94V-0 material and offers greater arc and t.. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
Sumitomo Bakelite North America 73-70-70 C-P /73-70-70 VO-P Short-Glass Reinforced Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SDG-F.I.. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
Plenco 7556 Phenolic, Briquette, Transfer Molded PLENCO 07556 is a glass fiber reinforced novolac phenolic molding compound, with good physical strengths and heat resistance along with excellent dimensional stability. UL recognized under component.. |
|||
Tensile Strength, Ultimate | 76.0 MPa @Temperature 200 °C |
11000 psi @Temperature 392 °F |
ISO 527-1/-2 |
DSM Stanyl® TW271B3 (PA46+PTFE)-CF15 15% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM Data |
Dow Tyril® 880B SAN TYRIL® 880B SAN copolymer combines the high levels of chemical resistance, heat resistance and overall strength of 880 resin with improved mold flow and mold release characteristics.Data provided b.. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D638 |
Adell BS-30 Nylon 6, General Purpose Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D638 |
Applied Composites 8038 Polyester SMC Industry Application: TransportationProduct Application: Mass TransitDistinct Features: Low Smoke Construction and Mass Transit, Oxygen Matex 80+, E84-61 TunnelInformation provided by Applied Compos.. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ASTM D638 |
Applied Composites 8041 Polyester SMC Industry Application: ElectricalProduct Application: Business MachinesDistinct Features: UL 94-VO, Radiant Panel |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 213 Polystyrene, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D638 |
A. Schulman ComAlloy Lubrilon® 511 Polycarbonate, Glass Fiber/PTFE, UL Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | ATSM D638 |
Ashley Polymers Ashlene® 520 Nylon 66 A general purpose basic Nylon 66 resin, slightly lubricated.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | Static |
Channel Industries 5600 Lead Zirconate Titanate Piezoelectric Navy Type VCharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most extens.. |