Polymer Property : Tensile Strength, Ultimate = 111000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	765 MPa	111000 psi	Outokumpu Typical, Cold Rolled Strip/Sheet; EN 10002-1
Outokumpu 4318 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled strip/sheet (CPP) and cold rolled strip sheet forms.
Tensile Strength, Ultimate	766 MPa @Temperature 649 Â°C	111000 psi @Temperature 1200 Â°F
Kennametal Stellite StelliteÂ® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes HastelloyÂ® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095Â°C, and good carburization resistance. Applications includ..
Tensile Strength, Ultimate	767 MPa	111000 psi
Haynes HR-160Â® alloy, hot rolled and solution annealed plate Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes MultimetÂ® alloy, 25.4-50.8 mm forged bar, 1185Â°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Ultimate	768 MPa	111000 psi
Haynes MultimetÂ® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Ultimate	765 MPa @Temperature 315 Â°C	111000 psi @Temperature 599 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes HastelloyÂ® C-22Â® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	762 MPa @Temperature 23.0 Â°C	111000 psi @Temperature 73.4 Â°F
Special Metals INCOLOYÂ® alloy 832 Stainless Steel INCOLOYÂ® alloy 832 is a low cost stainless steel developed specifically for domestic and industrial sheathed heater applications. With specific chemistry additions to ensure satisfactory formula..
Tensile Strength, Ultimate	767 MPa	111000 psi	Hardened 1800°F, Tempered 1200°F
ATI Allegheny Ludlum 410 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Ultimate	767 MPa	111000 psi	Typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 649°C (1200°F) Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Ultimate	767 MPa	111000 psi
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..