Polymer Property : Tensile Strength, Ultimate = 115 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 - 115 MPa
6530 - 16700 psi
Average value: 71.4 MPa Grade Count:11
Overview of materials for PET + PBT Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Tensile Strength, Ultimate 115 - 115 MPa

@Temperature 125 - 125 °C
16700 - 16700 psi

@Temperature 257 - 257 °F
Average value: 115 MPa Grade Count:1
Overview of materials for Polyetheretherketone, PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate 39.6 - 115 MPa
5750 - 16700 psi
Average value: 57.3 MPa Grade Count:7
Overview of materials for Polyphenylene Ether, PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, PTFE Filled". Each property range of values reported is minimum and maximum values ..
Tensile Strength, Ultimate 65.0 - 115 MPa

@Temperature 60.0 - 120 °C
9430 - 16700 psi

@Temperature 140 - 248 °F
Average value: 92.5 MPa Grade Count:2
Overview of materials for Polycarbonate, Carbon Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v..
Tensile Strength, Ultimate 35.0 - 115 MPa

@Temperature -40.0 - 100 °C
5080 - 16700 psi

@Temperature -40.0 - 212 °F
Average value: 70.0 MPa Grade Count:1
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum ..
Tensile Strength, Ultimate 100 - 115 MPa

@Temperature 130 - 175 °C
14500 - 16700 psi

@Temperature 266 - 347 °F
Average value: 101 MPa Grade Count:5
Overview of materials for Nylon 66, 40% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate 100 - 115 MPa

@Time 1.80e+7 - 7.20e+7 sec
14500 - 16700 psi

@Time 5000 - 20000 hour
Average value: 101 MPa Grade Count:5
Overview of materials for Nylon 66, 40% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate 86.2 - 115 MPa
12500 - 16700 psi
Average value: 101 MPa Grade Count:4
Overview of materials for Nylon 11 with 30% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are includ..
Tensile Strength, Ultimate 115 - 115 MPa

@Temperature -40.0 - -40.0 °C
16700 - 16700 psi

@Temperature -40.0 - -40.0 °F
Average value: 115 MPa Grade Count:1
Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced". Each property range of values repo..
Tensile Strength, Ultimate 20.0 - 115 MPa
2900 - 16700 psi
Average value: 53.0 MPa Grade Count:31
Overview of materials for Polypropylene, Glass Reinforced, Impact Modified
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Glass Reinforced, Impact Modified". Each property range of values reported is minimum and..
Tensile Strength, Ultimate 62.1 - 115 MPa
9000 - 16700 psi
Average value: 96.0 MPa Grade Count:12
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc..
Tensile Strength, Ultimate 24.1 - 115 MPa

@Temperature 60.0 - 175 °C
3500 - 16700 psi

@Temperature 140 - 347 °F
Average value: 61.3 MPa Grade Count:3
Overview of materials for Polyphthalamide (PPA), Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Mineral Filled". Each property range of values reported is minimum and maximum values o..
Tensile Strength, Ultimate 22.0 - 115 MPa
3190 - 16700 psi
Average value: 60.9 MPa Grade Count:150
Overview of materials for Polypropylene with 20% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are i..