Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester SMC (Compression), 30 wt.% glass Polyester thermosets are available in many formulations. They can be formulated for good to excellent resistance to acids, weak alkalis, and organic solvents. However, they are not recommended for u.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cookson Group Plaskon® 3300SGH Mineral Filled Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Exhibits exceptional reliability, excellent moldability, good release characteristics, low flash and rapid cure. This compound i.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
IDI Composites C-108 Thermoset Polyester, Molding Vinylester compounds in a range of strengths with superior corrosion resistance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by G.. |
|||
Tensile Strength, Ultimate | 82.7 MPa @Temperature 427 °C |
12000 psi @Temperature 800 °F |
Stainless Steel (18-8) butt joint |
Lucas-Milhaupt EASY FLO Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wettin.. |
|||
Tensile Strength, Ultimate | 83.0 MPa @Temperature 1095 °C |
12000 psi @Temperature 2003 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
Styron EMERGEâ„¢ 4202-8 MFR Polycarbonate EMERGEâ„¢ PC 4202-8 advanced resin is 20% glass reinforced polycarbonate containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. Ap.. |
|||
Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | ASTM Data |
Styron Pulse® 759 ABS + Polycarbonate, 15% Glass Reinforced PULSE® 759 Engineering resin is a 15% glass reinforced resin designed to provide excellent processability, high heat resistance, and practical toughness. PULSE 759 Engineering resin has been used.. |
|||
Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | ASTM D638 |
Techmer ES Electrafil® J-1200/CF/10 ABS, 10% Carbon Fiber Reinforced |
|||
Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | ASTM Data |
Styron CALIBRE™ 5201 15 Polycarbonate, 20% Glass Reinforced CALIBRE® 5201 is a 20% glass reinforced polycarbonate resin containing mold release for optimal processing. CALIBRE 5201 resin exhibits high modulus and excellent dimensional stability.CALIBRE 52.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E4940 Mineral & Glass Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E486 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E487 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 82.73 MPa | 12000 psi | |
Abatron AboCast/AboCure 8109-1 High melting point.Processing: 100/30 pbw; mix at 130-140°C (270 °F); cures in 16 h/120°C (250°F), 10 h/140°C (285°F), 8 h/160°C (320°F), 2 h/ 200°C (390°F).Applications: Heavy duty castin.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 520MS/520SMS Nylon 66, MoS2 Filled A general purpose Molybdenum-disulfide filled nylon resin.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 528LS Nylon 66 A general purpose Nylon 66, lubricated and heat stabilized for injection molding.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® N541L Nylon 66 A general purpose injection molding grade for heavy parts.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® P1525B Polycarbonate A rigid flame retardant black polycarbonate, for applications requiring superior dimensional stability and overall toughness.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Chem Polymer Chemlon 100 X Nylon 66, Lubricated GP A medium viscosity, general purpose injection molding grade nylon 66. Internally and externally lubricated for excellent feed and mold release properties.Data provided by the manufacturer, Chem Pol.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 431 Glass Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 1420B Polycarbonate, 20% Glass Reinforced A 20% glass reinforced polycarbonate for increased mechanical strength and thermal properties, modified for good impact with increased dimensional stability and overall toughness. 1423B with UV sta.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | Static |
Channel Industries 5804 Lead Zirconate Titanate Piezoelectric Navy Type IIICharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most exte.. |