- Polymer Property : Tensile Strength, Ultimate = 128000 psi
Polymer Property : Tensile Strength, Ultimate = 128000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 883 MPa @Temperature 600 °C |
128000 psi @Temperature 1110 °F |
|
| Kennametal Stellite Nucalloy® 453 High-Silicon Nickel-Base Hardfacing Alloy Applications include chemical control valves, nuclear globe valves, nuclear gate valves, nuclear sliding parts, and pressure bars for plywood cutters.Nucalloy® alloys are unique, patented, high-s.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Tensile Strength, Ultimate | 885 MPa @Temperature 650 °C |
128000 psi @Temperature 1200 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Tensile Strength, Ultimate | 883 MPa | 128000 psi | |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes Hastelloy® W alloy, shielded metal arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Ultimate | 880 MPa | 128000 psi | |
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 880 MPa | 128000 psi | |
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Tensile Strength, Ultimate | 880 MPa | 128000 psi | |
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Tensile Strength, Ultimate | 880 MPa | 128000 psi | Annealed |
| Special Metals INCONEL® Alloy 625 Niobium content includes tantalum. A nickel-chromium-molybdenum alloy with an addition of niobium that acts with the molybdenum to stiffen the alloy's matrix and thereby provide high strength witho.. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 21-2N Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 21-4N (JIS SUH35) Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 21-4NNb Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 23-8N Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 422 (JIS SUH616) Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel SUE52 Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | 885 - 925 MPa | 128000 - 134000 psi | |
| CLAL-MSX DECLAFOR® 1015 TH3 Wire quenched/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn.. |
|||
| Tensile Strength, Ultimate | 880 - 1000 MPa | 128000 - 145000 psi | |
| CLAL-MSX NICLAFOR® 1000 TDX Quenched/Cold Rolled, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
| Tensile Strength, Ultimate | 880 - 980 MPa | 128000 - 142000 psi | |
| CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel 214NS (JIS SUH36) Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | >= 882.6 MPa | >= 128000 psi | |
| Crucible Steel SIL 10N Martensitic Steel Information provided by Crucible Specialty Metals. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Tensile Strength, Ultimate | 883 MPa | 128000 psi | |
| HP Alloys Alloy 718, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internatio.. |
|||
| Tensile Strength, Ultimate | 885 MPa | 128000 psi | |
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 880 MPa | 128000 psi | |
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||