Polymer Property : Tensile Strength, Ultimate = 195 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 195 MPa
28300 psi
ASTM D638
Solvay Specialty Polymers Ryton® R-4XT Polyphenylene Sulfide Compound  (Unverified Data**)
Natural Color Polyphenylene Sulfide CompoundRyton® R-4XT is a 40% fiberglass reinforced polyphenylene sulfide compound that takes advantage of state-of-the-art polymerization technology to improve ..
Tensile Strength, Ultimate 195 MPa

@Temperature 980 °C
28300 psi

@Temperature 1800 °F
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate 195 MPa

@Temperature 980 °C
28300 psi

@Temperature 1800 °F
Haynes 25 alloy, vacuum investment castings, solution treated
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate 195 MPa

@Temperature 980 °C
28300 psi

@Temperature 1800 °F
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate 195 MPa
28300 psi
dry; ISO 527-1/-2
DSM Stanyl® TS250F8 PA46-GF40 FR
40% Glass Reinforced, Flame Retardant, Heat Stabilized
Tensile Strength, Ultimate 195 MPa
28300 psi
5mm/min; ISO 527
BASF Ultramid® N-333 NF3001 33% Glass Filled PA66 (Dry)
Ultramid N-333 NF3001 is a 33% glass reinforced, heat stabilized, injection molding PA66 uncolored.
Tensile Strength, Ultimate 195 MPa
28300 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 625 Nylon 6/6, Glass Reinforced
Data provided by the manufacturer, ComAlloy International Company.50% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 195 MPa
28300 psi
Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® 8233G 33% Glass-Filled Nylon 6 (Dry)  (discontinued **)
Capron 8233G is a 33% glass fiber reinforced polyamide 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in he..
Tensile Strength, Ultimate 195 MPa
28300 psi
ASTM D638
Chevron Phillips Xtel® XK2240 Polyphenylene Sulfide Alloy  (discontinued **)
Natural Color Polyphenylene Sulfide AlloyXtel™ XK2240 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength with an unique blend of tough..
Tensile Strength, Ultimate 195 MPa
28300 psi
ASTM D638
Solvay Specialty Polymers Ryton® R-4-200NA Polyphenylene Sulfide Compound  (Unverified Data**)
Natural Color Polyphenylene Sulfide CompoundRyton® R-4-200NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low mainten..