Polymer Property : Tensile Strength, Ultimate = 25.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM D638
North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc.
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM Data
Americas Styrenics Styron® 8100 MFD High Impact Polystyrene (discontinued **) STYRON 8100 MFD high impact polystyrene is designed for microfloppy diskettes (MFD) applications. It offers easy processing, coloring, abrasion resistance, impact strength, and high heat resistance...
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM D638
Total Finaclear® 530 Clear Impact Polystyrene (discontinued **) Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other..
Tensile Strength, Ultimate	25.0 MPa	3630 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman M2004-P Polyethylene (discontinued **) M2004-P polyethylene is suggested for applications such as spiral-wound can linings, release paper and photographic paper. M2004-P has been found to exhibit good barrier properties, temperature res..
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM D638
NOVA Chemicals Sclair® 96A HDPE Extrusion Resin (discontinued **) Features: Excellent processability, excellent stretchability, superior strength, gel free.Applications: Oriented tapes for industrial woven bags and tarpaulins, monoaxial oriented films.Data provide..
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM D638
NOVA Chemicals Sclair® 96A-UV8D HDPE Extrusion Resin (discontinued **) Features: Excellent processability, excellent stretchability, superior strength, gel free, excellent UV resistance.Applications: Oriented tapes for industrial woven bags and tarpaulins, monoaxial or..
Tensile Strength, Ultimate	25.0 - 25.0 MPa @Temperature 60.0 - 60.0 °C	3630 - 3630 psi @Temperature 140 - 140 °F	Average value: 25.0 MPa Grade Count:1
Overview of materials for Polycarbonate, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 10% Glass Filled". Specific grades with glass content between 5% and 14% are included. Ea..
Tensile Strength, Ultimate	25.0 - 317 MPa	3630 - 46000 psi	Average value: 133 MPa Grade Count:19
Overview of materials for Polypropylene, Fiber Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Fiber Grade". Each property range of values reported is minimum and maximum values of app..
Tensile Strength, Ultimate	25.0 - 45.0 MPa	3630 - 6530 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 1015/0078 PVDF Homopolymer (discontinued **) Key features of this grade: Plasticized, Offshore, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorina..
Tensile Strength, Ultimate	25.0 - 178 MPa @Temperature -40.0 - 150 °C	3630 - 25800 psi @Temperature -40.0 - 302 °F	Average value: 66.1 MPa Grade Count:9
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	25.0 - 82.7 MPa	3630 - 12000 psi	Average value: 60.5 MPa Grade Count:4
Overview of materials for Nylon 6, Stainless Steel Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Stainless Steel Filled". Each property range of values reported is minimum and maximum values o..
Tensile Strength, Ultimate	25.0 - 400 MPa @Strain 1.00 - 10.0 %	3630 - 58000 psi @Strain 1.00 - 10.0 %	Average value: 101 MPa Grade Count:5
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	25.0 - 195 MPa @Temperature 60.0 - 120 °C	3630 - 28300 psi @Temperature 140 - 248 °F	Average value: 128 MPa Grade Count:1
Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. ..
Tensile Strength, Ultimate	25.0 MPa @Temperature 22.0 Â°C	3630 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® BMC 2600 Unsaturated Polyester UP BMC 2600 is a special BMC with reduced electrical properties. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. Because of its improved..
Tensile Strength, Ultimate	25.0 - 34.0 MPa	3630 - 4930 psi
Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer.
Tensile Strength, Ultimate	25.0 - 36.0 MPa	3630 - 5220 psi
Cosmic Plastics ID-50 Dacron Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer.
Tensile Strength, Ultimate	25.0 - 35.0 MPa	3630 - 5080 psi	ASTM D638
Zeus PFA Tubing PFA, or perfluoroalkoxy, is well recognized for its ability to maintain mechanical integrity in extreme temperatures even when exposed to caustic chemicals. PFA comes in high purity versions that ar..
Tensile Strength, Ultimate	25.0 - 34.0 MPa	3630 - 4930 psi
Cosmic Plastics ID-40 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer.
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ISO 527-1
Chengdu Polyster FH5550 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H5550 and self-made flame retardant material. Flame retardant, good balance of low and high temperature properties. Applications requiring flame retardancy, such as wires, cables and optica..
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ISO 527-1
Chengdu Polyster H4040 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent flex resistance, especially at low temperatures. Moldable even in thin sections. Can be used in light..
Tensile Strength, Ultimate	25.0 - 40.0 MPa	3630 - 5800 psi
Alliance BIN-45 Bonded (Composite) Magnetic Material
Tensile Strength, Ultimate	25.0 - 40.0 MPa	3630 - 5800 psi
Alliance BIN-72 Bonded (Composite) Magnetic Material
Tensile Strength, Ultimate	25.0 MPa	3630 psi	ASTM D638
A. Schulman ComAlloy Comtuf® 164 Polypropylene, Mineral Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
Tensile Strength, Ultimate	25.0 - 215 MPa @Temperature -55.0 - 275 °C	3630 - 31200 psi @Temperature -67.0 - 527 °F	Average value: 109 MPa Grade Count:18
Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum..
Tensile Strength, Ultimate	25.0 - 30.0 MPa @Temperature 60.0 - 60.0 °C	3630 - 4350 psi @Temperature 140 - 140 °F	Average value: 28.3 MPa Grade Count:3
Overview of materials for Acetal Copolymer, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Glass Bead Filled". Each property range of values reported is minimum and maximum valu..
Tensile Strength, Ultimate	25.0 - 325 MPa	3630 - 47100 psi	Average value: 114 MPa Grade Count:222
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M..
Tensile Strength, Ultimate	25.0 MPa	3630 psi	DIN 53504
Lubrizol ESTANE® 58213 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..