Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.6 - 145 MPa | 4000 - 21000 psi | Average value: 55.7 MPa Grade Count:33 |
Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | Average value: 34.4 MPa Grade Count:11 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "ABS + Glass Blend". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Rostone Rosite® 3552C BMC Thermoset Polyester, 15% Glass Reinforced
(discontinued **) Key Features: High Stability, Non-OutgassingDesigned for applications requiring excellent stability and dimensional control. Out-gassing is virtually eliminated making it ideal for systems such as .. |
|||
Tensile Strength, Ultimate | 27.6 - 186 MPa | 4000 - 27000 psi | Average value: 139 MPa Grade Count:22 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | Reinforced |
Natural Rubber, Not Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | 2 in/min.; ASTM D638 |
Ineos K44-06-122 HDPE HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as .. |
|||
Tensile Strength, Ultimate | >= 27.6 MPa | >= 4000 psi | ISO 1184-1983E |
LyondellBasell DP 0110M Polybutene Key Features: highly isotactic, semi-crystalline nucleated homopolymer, good creep resistance, good environmental stress crack resistance, FDA acceptable, easily dispersibleApplications: packaging i.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | |
Williams Advanced Alloys WS314A Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412 |
Lubrizol Estane® CP80AS2 Thermoplastic Polyurethane Type: Estane® CP80AS2 is a soft, polyester based thermoplastic polyurethane resin.Features: Outstanding compatibility with flexible PVC allowing easy dispersion without pre-compounding.Uses: Tube/H.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412/D638 |
Lubrizol Estane® MVT 80AF3 Thermoplastic Polyurethane, Moisture Vapor Transmission Type: Estane® MVT 80AF3 TPU is a aromatic polyether-based thermoplastic polyurethane (TPU).Features: High moisture vapor transmission, good low temperature properties and elasticity.Uses: Blown and.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
American Polymers API 545 Polystyrene API 545 is a high impact, high heat resistant grade of impact modified polystyrene. This material features fast set-up as well as easy colorability.Applications: API 545 is suggested for heavy part.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Eastman Tenite Propionate 380A2R30018 Natural, Trsp Cellulose Acetate Propionate Plasticizer 18%. Weight loss on heating = 1% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pro.. |
|||
Tensile Strength, Ultimate | 27.6 MPa @Temperature 927 °C |
4000 psi @Temperature 1700 °F |
|
Crucible Steel 430 Chromium Steel Crucible 430 is essentially a non-hardenable chromium steel which is adaptable for general purpose corrosion and heat resisting applications. It is prone to slight hardening by heat treatment. This.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM Data |
Dow Prevail® 3100 ABS + Polyurethane PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D638 |
Buckeye Polymers BP RPPC 0510 Blk Reprocessed Polypropylene, Unfilled This reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin compounds are utilize.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® PP5063 Polypropylene, Injection Grade Bapolene PP5063 is a high clarity Natural PP Random Copolymer for injection molding. This resin exhibits excellent clarity and low temperature impact properties. This product meets FDA standards f.. |
|||
Tensile Strength, Ultimate | 27.6 MPa @Temperature 982 °C |
4000 psi @Temperature 1800 °F |
Transverse |
AK Steel NITRONIC® 19-D Duplex Stainless Steel AK Steel NITRONIC® 19D is a stainless steel with a mixed ferrite and austenite structure. This alloy provides high yield strength (65 ksi minimum {448 MPa}),
good drawing and welding characteristi.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 501E Mineral Filled, Glass Reinforced Polyester BMC 501E molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression and transfer molding. It is a product with good overall electrical properties, flame.. |
|||
Tensile Strength, Ultimate | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
Bulk Molding Compounds BMC 604 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 604 molding compound is a low-cost, mineral filled glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is a general purpose material wit.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 902 Thermoset Polyester, Soft Flow Encapsulation Grade BMC 902 is a medium strength, high flow molding compound that meets Ford Specification ESFM3D114- A. BMC 902 has excellent electrical properties and creep resistance. It can be pigmented in a wide r.. |
|||
Tensile Strength, Ultimate | 27.6 - 34.5 MPa | 4000 - 5000 psi | |
Bulk Molding Compounds BMC 1410 Electrical Grade BMC 1410 is a high-strength electrical grade material with excellent flammability resistance. In most applications, this material is competitive with SMC. Equal performance at a lower cost. Normally.. |
|||
Tensile Strength, Ultimate | 27.6 - 55.2 MPa | 4000 - 8000 psi | |
Bulk Molding Compounds BMC 324 Automotive Grade Molding Compound BMC 324 is a low profile, automotive grade molding compound that is suitable for Injection, Compression or Transfer molding operations. BMC 324 can be metallized directly, without an initial base-co.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1300 Black Unfilled Electronic Grade Epoxy Encapsulant Resinlab™ EP1300 Black (Formerly Lab Product W092602) is a two part unfilled electronic grade epoxy encapsulant designed for small to medium sized castings. It has a pot life of about one hour and .. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, General Description
(discontin Product form is white, odorless chips. Distinguishing Feature: Low viscosity polymer. Improves processing of dry stiff stocks.35 % Chlorine Content. 1% Sulfur Content. Excellent Abrasion Resista.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, General Description
(disconti Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Good green strength. Improves processing of soft or highly extended stocks.36 % Chlorine Content. 1% Sulfur.. |
|||
Tensile Strength, Ultimate | <= 27.6 MPa | <= 4000 psi | With carbon black or gum stocks. ASTM D412-80 |
DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, General Description
(discontinu Product form is white, odorless chips. Distinguishing Feature: High polymer viscosity. Excellent oil and fluids resistance. High uncured strength.43 % Chlorine Content. 1% Sulfur Content. Excel.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1046FG Black Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Black is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | TM R050-36 |
Resinlab® EP1190 Flame Retardant Epoxy Casting Resin Resinlab™ EP1190 is a medium viscosity, flame retardant epoxy casting resin system. It is recognized under the Component Recognition Program of Underwriters Laboratories Inc., (File# E186034, Proje.. |