Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM Data |
Americas Styrenics Styron® XL-8028 High Impact Polystyrene
(discontinued **) STYRON® XL-8028 high impact polystyrene is designed for VCR cassettes, toys, small appliances, telephones, housewares, tool items, computer consoles and bodies for computer cartridges. It offers hi.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
ExxonMobil Escorene® LL-5002 LLDPE Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A linear low density polyethylene resin designed to provide good processability and ease of blending. LL-5002 also exhibits good toughness and envi.. |
|||
Tensile Strength, Ultimate | 21.0 - 30.0 MPa | 3050 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 61010 PVDF Copolymer
(discontinued **) Key features of this grade: Permanent Plasticizing, Fuel Line, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF i.. |
|||
Tensile Strength, Ultimate | 21.0 - 75.8 MPa | 3050 - 11000 psi | Average value: 56.7 MPa Grade Count:15 |
Overview of materials for Fluorocarbon ETFE, with Glass or Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Fluorocarbon ETFE, with Glass or Carbon Fiber Filler". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
LyondellBasell Astryn BE17FC Polypropylene Copolymer, 40% Calcium Carbonate Key Features: fractional melt flow, medium high modulus, UV-stabilized, mineral-filled, blow molding and extrusion grade polypropylene copolymer, excellent impact and stiffness balance, good melt st.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
LyondellBasell Astryn SD068-4 Polypropylene Copolymer, 40% Calcium Carbonate Key Features: fractional melt flow, high modulus, mineral-filled, blow molding and extrusion grade polypropylene copolymer, good melt strength, excellent processability, excellent impact and stiffne.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 391E Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.Ap.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 391E Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer DescriptionFormion® FI 1051E is a non-reinforced, transparent, extrusion grade Sodium Ionomer. It has been formulated for high durability, cut and puncture resistance, and low temperature ductilit.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 389 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 391E Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | Dynamic tensile strength |
Channel Industries 1300 Barium Titanate Piezoelectric Navy IV typeModified barium titanates are widely used in transducers requiring moderate power level and receiving sensitivity. Special characteristics have made barium titanate a proven material for.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ISO 527-1/-2 |
DSM Arnitel® EB464-01 TPC-ET Antisqueak Blow Molding Grade |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 21.0 - 48.0 MPa | 3050 - 6960 psi | Average value: 33.2 MPa Grade Count:11 |
Overview of materials for Ethyl Cellulose, Molded This property data is a summary of similar materials in the MatWeb database for the category "Ethyl Cellulose, Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | Cured 7 min at 177°C and Post Cured 16 hr at 232°C |
DuPont Performance Polymers GBL-200 Formulation
(discontinued **) FormulationViton® GBL-200 |