Polymer Property : Tensile Strength, Ultimate = 430 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	430 MPa @Temperature 200 °C	62400 psi @Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4311 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Tensile Strength, Ultimate	430 MPa @Temperature 100 °C	62400 psi @Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4401 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Tensile Strength, Ultimate	430 MPa @Temperature 100 °C	62400 psi @Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Tensile Strength, Ultimate	430 MPa @Temperature 500 °C	62400 psi @Temperature 932 °F	EN min.; EN 10002-5
Outokumpu 4429 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), cold rolled strip/sheet and rod forms.
Tensile Strength, Ultimate	430 MPa @Temperature 100 °C	62400 psi @Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4436 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Tensile Strength, Ultimate	430 MPa @Temperature 200 °C	62400 psi @Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Ultimate	430 MPa @Temperature 200 °C	62400 psi @Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Ultimate	430 MPa @Temperature 200 °C	62400 psi @Temperature 392 °F	EN min.; EN 10002-5
Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o..
Tensile Strength, Ultimate	>= 430 MPa	>= 62400 psi
MetalTek MTEK HK40 Cast UNS J94204 Heat Resistant Stainless Steel Increased strength for more highly stressed applications. Good resistance to oxidizing or reducing process flow.Applications: Calcining tubes, pier caps, high temperature fixtures and hardware.Infor..
Tensile Strength, Ultimate	>= 430 MPa	>= 62400 psi
MetalTek MTEK 25-35 Cast UNS N08705; Cast UNS J95705 Heat Resistant Stainless Steel Higher chrome and nickel content provides increased strength and resistance to both oxidation and carburization.Applications: Reformer and Ethylene pyrolysis tubes and fittings.Information provided ..
Tensile Strength, Ultimate	430 MPa @Temperature 300 Â°C	62400 psi @Temperature 572 Â°F	Annealed prior to test
Special Metals NILOÂ® Alloy 36 Low-Expansion Alloy Inflection point 220Â°C. A nickel-iron low-expansion alloy containing 36% nickel. It maintains nearly constant dimensions over the range of normal atmospheric temperatures, and has a low coeffic..
Tensile Strength, Ultimate	430 MPa @Temperature 300 Â°C	62400 psi @Temperature 572 Â°F	Annealed prior to test
Special Metals NILOÂ® Alloy 42 Controlled-Expansion Alloy Inflection point 370Â°C. A nickel-iron controlled-expansion alloy containing 42% nickel. It has a low and nominally constant coefficient of thermal expansion from room temperature to about 570Â..
Tensile Strength, Ultimate	430 - 550 MPa	62400 - 79800 psi
SSAB Tunnplat DomexÂ® 355MC HSLA Steel HSLA SteelCharacteristics: For hot-dip galvanizing, a thin Zn coating (50-80 microns) is specified.DomexÂ® MC grade steels conform to the provisions of EN 10149-2 standard and often have better pr..
Tensile Strength, Ultimate	430 - 500 MPa	62400 - 72500 psi
CLAL-MSX CUPROROR® TL4 Hard, Copper Alloy Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat..