Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 45.0 - 115 MPa | 6530 - 16700 psi | Average value: 71.4 MPa Grade Count:11 |
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
PolyOne Stat-Tech™ AS-7SS/000 ABS - 7% Stainless Steel Fiber
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 45.0 - 118 MPa | 6530 - 17100 psi | Average value: 93.7 MPa Grade Count:90 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Tensile Strength, Ultimate | 45.0 - 138 MPa | 6530 - 20000 psi | Average value: 93.7 MPa Grade Count:35 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled". Each property range of values repor.. |
|||
Tensile Strength, Ultimate | 45.0 - 134 MPa | 6530 - 19500 psi | Average value: 76.3 MPa Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS), Aramid Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Aramid Fiber". Each property range of values reported is minimum and maximu.. |
|||
Tensile Strength, Ultimate | 45.0 - 174 MPa | 6530 - 25200 psi | Average value: 102 MPa Grade Count:142 |
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 45.0 - 45.0 MPa @Temperature 60.0 - 60.0 °C |
6530 - 6530 psi @Temperature 140 - 140 °F |
Average value: 45.0 MPa Grade Count:1 |
Overview of materials for Nylon 66/6 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6". Each property range of values reported is minimum and maximum values of appropriate MatWeb .. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Plenco 5440 Black General Purpose Phenolic Molding Compound
(discontinued **) Plaslok 5440 is the replacement material for the former Union Carbide BMRS-5440. It is a two-stage, phenolic molding compound that has been successfully formulated to accommodate a very wide range .. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Plenco 504 Black (COM) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound
(discontinued **)< Plaslok 504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding compounds. Since it also has good electrical.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | |
Kraton® G1657 + PA-6,6 blend (12/8/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | |
Kraton® G1657 + PA-6,6 blend (8/12/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO 527 |
Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH50 Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities a.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Tipco Tipcolite® TMS 211 Phenolic Compound, Cotton, Filler & Wood Flour, having Medium Flow & High Strength Medium Flow Phenolic Compound, Reinforced with Cotton, Filler & Wood FlourApplications: Industrial & AutomotivesProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industr.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO 527 |
Wellman Wellamid® XT1482-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Tensile Strength, Ultimate | 45.0 MPa @Temperature 100 °C |
6530 psi @Temperature 212 °F |
ISO 527-2 |
Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced Xmod GD301HP is reinforced with 32% chemically coupled glass fibers and based on specific Polymer matrix material which is bringing excellent mechanical properties (impact behavior) and very good st.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | cond; ISO 527-1/-2 |
DSM Akulon® K222-KGV4 /A PA6-GF20 FR(30) 20% Glass Reinforced, Heat Stabilized, Flame Retardant (Halogen-phosphorous-free) |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Cresset Powers Cress-Alon™ NE6040-ST 4% Nano Clay Loaded, 6.0 r.v. Super Tough Grade Nylon 6, 50% RH Surpasses super tough neat resins in strength, heat resistance, and hardness.Information provided by Cresset Powers Ltd. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM Data |
Dow Tyril® 125 SAN Dow TYRIL® 125 resin is specially formulated for blending and is an ideal carrier material for use in making color concentrates. It offers high melt flow and excellent chemical resistance.Data prov.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO R527 |
Arkema Group Orgalloy® RS 60E10 Polyamide Alloy Polyamide Alloy, Rigid Blown film gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ATSM D638 |
Ashley Polymers Ashlene® 261WO PPO A general purpose V-0 rated resin with good impact strength.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 45.0 - 105 MPa | 6530 - 15200 psi | Average value: 69.6 MPa Grade Count:8 |
Overview of materials for Nylon 66/6, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, Mineral Reinforced". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
PolyOne Lubri-Tech™ AT-000/15T-2S Copolymer Acetal - 15% PTFE, 2% Silicone Lubricated
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 45.0 - 45.0 MPa @Time 605000 - 605000 sec |
6530 - 6530 psi @Time 168 - 168 hour |
Average value: 53.1 MPa Grade Count:1 |
Overview of materials for Thermoplastic Polyurethane (TPUR), Polyester Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane (TPUR), Polyester Grade". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO 527-1, 2 |
Polyplastics Duracon® SF-10 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Plaslok 7000 Black General Purpose Woodflour Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 7000 is the replacement material for .. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Plaslok 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use. Plaslok 306 is a two-stage, mineral and flock.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Sumitomo Bakelite North America FM 1132P Cellulose Reinforced Phenolic Novolac FM 1132P is a two-stage phenolic molding compound reinforced with cellulose in pellet form. FM-1132P is recommended to customers desiring approval under ASTM D-5948-96,Type CFI-10. (Replaces Militar.. |
|||
Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
Plaslok 501 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 501 is a two-stage, mineral and flock.. |
|||
Tensile Strength, Ultimate | 45.0 - 110 MPa @Temperature 60.0 - 150 °C |
6530 - 16000 psi @Temperature 140 - 302 °F |
Average value: 73.8 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Fiber Filled". Each property range of values reported is minimu.. |