Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 33.1 MPa
4800 psi
TM R050-36
Resinlab® EP1325 Thixotropic, Heat Curing Epoxy Adhesive
Resinlab™ EP1325 and EP1325LV are one part thixotropic, heat curing epoxy adhesives. They can also be used as a small mass potting compounds, staking or damming adhesives, or polymer systems where ..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Butyrate 465E2R30012 Natural, Trsp Cellulose Acetate Butyrate  (discontinued **)
Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 - 203 MPa
4800 - 29400 psi
Average value: 140 MPa Grade Count:27
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638-95
Multibase Multi-ABS 802 Utility Grade White
Data provided by Multibase.
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM Data
Styron Magnumâ„¢ 2620 ABS, Impact Grade
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM Data
Styron Magnumâ„¢ 357HP ABS, High Heat
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
Williams Advanced Alloys WS280 Solder
All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPH 3230 Polypropylene, Blow Molding Grade
Homopolymer blow molding gradeLubricated - Fina 3230 offers superior core rod release, eliminating the need for additional lubricant.High Purity - Fina 3230 features minimum taste and odor and optim..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPH 3429 Polypropylene, Injection Molding Grade
LTHA injection molding homopolymerLTHA - FINA 3429 is engineered with an LTHA additive system that gives excellent leach resistance in hot/wet environments that contain bleach and laundry detergents..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPH 3622 Polypropylene, Injection Molding Grade
General purpose injection molding and extrusion homopolymerGood Processability -- FINA 3622 is engineered for good processability in thin wall multi- cavity molds.Good Clarity -- FINA 3622 has good ..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPH 3727WZ Polypropylene, Injection Molding Grade
Fina’s new HIGH PERFORMANCE injection molding gradeBalanced Properties - Fina 3727WZ strikes an optimum balance between excellent mechanical properties (tensile, flex and impact) and processability..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPR 3230XZ Polypropylene, Blow Molding Grade
Homopolymer Blow Molding GradeLubricated – FINA 3230XZ offers superior core road release, eliminating the need for additional lubricant.Antistat – FINA 3230XZ contains antistat to minimize dust ac..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Total PPH 3825 Polypropylene, Injection Molding Grade
Easy flow injection molding homopolymerEasy Flow - FINA 3825 exhibits exceptionally easy flow characteristics.FDA - FINA 3825 complies with all applicable FDA regulations for food contact applicatio..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Acetate 105E1R26033 Clear, Trsp Cellulose Acetate
Plasticizer 29%. Weight loss on heating = 2.6% per ASTM D 707. Soluble matter loss = 0.4% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Butyrate 530A3720016 Clear, Trsp Cellulose Acetate Butyrate
Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Propionate 350E0096912 Natural, Trsp Cellulose Acetate Propionate
Plasticizer 13%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Propionate 375E4000012 Clear, Trsp Cellulose Acetate Propionate
Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Propionate 376E4000012 Clear, Trsp Cellulose Acetate Propionate
Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Propionate 377E4861312 Clear, Trsp Cellulose Acetate Propionate
Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Eastman Tenite Propionate 383A2R30012 Natural, Trsp Cellulose Acetate Propionate
Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Adell EA-16 Homopolymer Polypropylene, 30% Talc Filled
Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate 33.1 MPa
4800 psi
TM R050-36
Resinlab® EP1056LV Black Urethane Modified Epoxy Casting Resin
Resinlab™ EP1056LV Black is a two part urethane modified epoxy casting resin designed to give good adhesion to metals and PVC. It has good wetting to most surfaces and is free-flowing to penetrate ..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
American Polymers API 425 Polystyrene
API 425 is a medium impact grade of polystyrene for injection molding. API 425 has good gloss, easy flow and fast cycling properties.Applications: API 425 is widely used in cosmetic packaging, food..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
TM R050-36
Resinlab® EP1285HD-10 Highly Filled, Medium Viscosity Casting Resin
Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM D638
Buckeye Polymers BP RPP 1010 T Polypropylene, 10% Mineral Filled
This Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistance, and resis..
Tensile Strength, Ultimate 33.1 MPa
4800 psi
ASTM Data
Styron Magnum™ 9020 ABS, High Gloss
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM AB..