Polymer Property : Tensile Strength, Ultimate = 496 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	496 MPa @Temperature 538 Â°C	71900 psi @Temperature 1000 Â°F
Haynes HastelloyÂ® G-30Â® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOYÂ® G-30Â® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid..
Tensile Strength, Ultimate	496 MPa @Temperature 760 Â°C	71900 psi @Temperature 1400 Â°F
Haynes HastelloyÂ® C-22Â® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	496 - 552 MPa	72000 - 80000 psi
Eagle Brass 220 Commercial Bronze, Extra Spring CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum..
Tensile Strength, Ultimate	496 - 552 MPa	72000 - 80000 psi
Eagle Brass 230 Red Brass, Extra Hard CDA 230 is known for having an electrical conductivity of 37% IACS, red color, corrosion resistance, excellent formability and moderate strength. Typical uses include costume jewelry, eyelets, faste..
Tensile Strength, Ultimate	496 - 600 MPa	72000 - 87000 psi
Eagle Brass 511 Phosphor Bronzes 4%, Hard 511 offers wear resistance, high strength, ductility, excellent spring properties and good bearing properties. Typical uses include fuse clips, switch parts, terminals, electronic connectors, bridge..
Tensile Strength, Ultimate	496 - 593 MPa	72000 - 86000 psi
Eagle Brass 519 Phosphor Bronzes 6%, 3/4 Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C..
Tensile Strength, Ultimate	496 MPa	72000 psi	Typical
Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for..
Tensile Strength, Ultimate	496 MPa @Temperature 427 °C	71900 psi @Temperature 801 °F
Carpenter 20-Mo6® Stainless Steel, Tensile Properties at 93°C Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, ..
Tensile Strength, Ultimate	496 MPa @Temperature 204 °C	71900 psi @Temperature 400 °F	Plate
AK Steel NITRONIC® 30 Austenitic Stainless Steel AK Steel NITRONIC 30 Stainless Steel offers significantly higher strength than Type 304 and potential for applications requiring good resistance to aqueous and atmospheric corrosion resistance combi..
Tensile Strength, Ultimate	496 MPa	71900 psi	Typical
ATI Allegheny Ludlum Type AL 441HP™ Stainless Steel Alloy Allegheny Ludlum stainless Type AL 441HP™ alloy is a heat resisting ferritic grade providing good oxidation and corrosion resistance for applications like automotive exhaust system components. Dua..