Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
NCMT NanoPAC™ G2050H High Performance Polypropylene Nanocomposite Applications: Construction MaterialInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 50.0 - 130 MPa @Temperature 125 - 275 °C |
7250 - 18900 psi @Temperature 257 - 527 °F |
Average value: 86.7 MPa Grade Count:1 |
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO 527 |
Eastman EASTALLOY Polymer DA105, Natural Alloy
(discontinued **) General: All ISO tests are run @ 4-mm thickness with the exception of Impact Resistance, which is run @ 2-mm thickness. Comments: Properties reported here are typical of average lots. Eastman ma.. |
|||
Tensile Strength, Ultimate | 50.0 MPa @Temperature 60.0 °C |
7250 psi @Temperature 140 °F |
ISO 527 |
LATI LATAN 13 G/15 15% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)
(discontinued **) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Tensile Strength, Ultimate | 50.0 - 80.0 MPa @Temperature 60.0 - 120 °C |
7250 - 11600 psi @Temperature 140 - 248 °F |
Average value: 66.7 MPa Grade Count:1 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 50.0 - 125 MPa @Temperature 0.000 - 160 °C |
7250 - 18100 psi @Temperature 32.0 - 320 °F |
Average value: 67.6 MPa Grade Count:4 |
Overview of materials for Polysulfone (PSU) This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 50.0 - 58.0 MPa | 7250 - 8410 psi | Average value: 55.3 MPa Grade Count:3 |
Overview of materials for Phenolic, Resole, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Mineral Filled". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 50.0 - 165 MPa | 7250 - 23900 psi | Average value: 111 MPa Grade Count:83 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Hannam Chemical Hanalac HU-600 ABS |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
Saint-Gobain Vitreosil® CFQ/TSC Optical Fused Quartz Vitreosil® CFQ/TSC grades are for use in less demanding applications including viewing windows for use in corrosive and high temperature environments and non-optical components such as spacers, i.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 3557 Phenolic, Granular, Compression Molded PLENCO 03557 is a woodflour and mineral filled phenolic molding compound offering excellent dielectric strength values at elevated temperatures while maintaining mechanical strength properties. UL r.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 7080 Phenolic, Nodular, Compression Molded PLENCO 07080 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength properties along with outstanding resistance to cracking and degradation from soap and de.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 7202 Phenolic, Granular, Injection Molded PLENCO 07202 is an organic fiber reinforced phenolic molding compound, formulated to offer improved mechanical strength properties with an industrial finish. UL recognized under component file E4065.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Tipco Tipcolite® THD 321 Phenolic Compound, Wood Flour & Cellulose, having Soft Flow & High Strength Soft Flow Phenolic Compound, Reinforced with Wood Flour & CelluloseApplications: Switchgear, HRC FusesProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industries Lt.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
Plenco 4301 Phenolic, Granular, Injection Molded PLENCO 04301 is a heat resistant, mineral filled phenolic molding compound offering excellent dimensional stability and electrical properties. UL recognized under component file E40654. 04301 is ava.. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | DIN 53504 |
Lubrizol ESTANE® 5701F1 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
Covestro Baydur® 110 FR Polyurethane Rigid microcellular RIM polyurethane material. Fast demold times; self releasing; long flow paths possible, therefore suitable for production of large moldings. Parts are injected through only one .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 |
Arkema Group Orgalloy® R 60 ES Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
Chang Chun Plastic PBT1100L General Purpose PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
Chang Chun Plastic PBT1200M General Purpose PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 - 150 MPa | 7250 - 21800 psi | Average value: 125 MPa Grade Count:18 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 50.0 - 80.0 MPa @Temperature 160 - 160 °C |
7250 - 11600 psi @Temperature 320 - 320 °F |
Average value: 70.2 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
PolyOne Lubri-Tech™ MP-000/15T Modified PPO - 15% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | |
Kraton® G1657 + PA-6 blend (16/4/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
Tensile Strength, Ultimate | 50.0 - 70.0 MPa | 7250 - 10200 psi | ASTM D638 |
Chang Chun Plastic PBT2100 Fire Retardant PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 50.0 - 90.0 MPa @Temperature 60.0 - 150 °C |
7250 - 13100 psi @Temperature 140 - 302 °F |
Average value: 71.3 MPa Grade Count:2 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |
|||
Tensile Strength, Ultimate | 50.0 - 55.0 MPa @Strain 1.00 - 1.70 % |
7250 - 7980 psi @Strain 1.00 - 1.70 % |
Average value: 78.5 MPa Grade Count:1 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |
|||
Tensile Strength, Ultimate | 50.0 - 359 MPa | 7250 - 52000 psi | Average value: 104 MPa Grade Count:18 |
Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Unreinforced, Extruded". Each property range of values reported is minimum .. |
|||
Tensile Strength, Ultimate | 50.0 - 103 MPa | 7250 - 15000 psi | Average value: 69.7 MPa Grade Count:7 |
Overview of materials for Polybutylene Terephthalate (PBT), Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Aramid Fiber Filled". Each property range of values reported is minimu.. |