Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
PTS Trimid® N66-S100L High Impact Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Ultimate | 51.0 - 69.0 MPa | 7400 - 10000 psi | Average value: 58.0 MPa Grade Count:10 |
Overview of materials for Phenolic, Resole, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN161 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
LyondellBasell Higlass SB224-2 Polypropylene Copolymer, 20% Glass Fiber Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, moderate rigidity, good processabilityApplications: of.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 1501 Polyester, Briquette, Transfer Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2000 Phenolic, Granular, Compression Molded PLENCO 02000 is a versatile general purpose, organic filled phenolic molding compound, offering optimum cure characteristics and an excellent balance of molding properties. UL recognized under compo.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2408 Phenolic, Granular, Compression Molded PLENCO 02408 is a general purpose, organic filled phenolic molding compound, offering excellent cosmetic characteristics and improved electrical strength properties. UL recognized under component fi.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2571 Phenolic, Granular, Transfer Molded PLENCO 02571 is a general purpose, organic filled phenolic molding compound offering optimum cure characteristics while maintaining excellent mechanical and electrical properties. UL recognized unde.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 3303 Phenolic, Granular, Compression Molded Plenco 03303 is a renumber of Plaslok 5303. Plenco 03303 is a two-stage, mineral and flock-filled phenolic molding compound offering excellent electrical insulating properties. It can be processed b.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 4349 Phenolic, Granular, Transfer Molded PLENCO 04349 is a heat resistant, mineral filled phenolic molding compound offering optimized cure characteristics, and excellent heat resistant properties. PLENCO 04349 is also formulated to offer .. |
|||
Tensile Strength, Ultimate | 51.0 MPa @Temperature -20.0 °C |
7400 psi @Temperature -4.00 °F |
Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 |
DuPont Elvax® 265 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Toyobo A1071D Thermoplastic Polyurethane Elastomer, Injection Grade Polybutyleneadipate type, the most general purpose type of Toyobo Polyurethane; features excellent cost-performance. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes,.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 37 |
Lubrizol ESTANE® 58134 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 527-1, 2 |
Polyplastics Duranex® 652SA Polybutylene Terephthalate (PBT), Low density, Low wear, Mineral filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman DURASTAR DS1010 Natural PCTA Copolyester DURASTAR DS1010 polymer contains a mold release. It has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Eastman Eastar Copolyester BR003, Natural PCTA Copolyester EASTAR BR003 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabiliti.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | DIN 53 504 |
Dow BETAMATE™ 5103-2 Epoxy BETAMATE™ 5103-2 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel, including coated ste.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Covestro Makroblend® EL 703 Polycarbonate + Polyester-based Blend, Impact Modified, Flame-Retardant, UV Stabilized Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 0.5 x 0.125 in. specimen; 0.2 in/min; ASTM D638 |
Americas Styrenics STYRON™ 668 General Purpose Polystyrene Resin STYRON™ 668 is a general purpose polystyrene with medium flow and a balance of heat resistance and stiffness characteristics that make it suitable for applications such as CD jewel boxes. STYRON™.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ATSM D638 |
Ashley Polymers Ashlene® 733LD Nylon 6 A modified injection molding grade nylon for applications requiring flexibility.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ATSM D638 |
Ashley Polymers Ashlene® P254WO PPO A general purpose V-0 rated resin with high impact strength.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 37-10/AboCure 37-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 45-10/AboCure 45-10 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | Typical averaged test results for Abatron Adhesive/Casting Resins. |
Abatron AboCast 53-15/AboCure 53-15 Adhesive/Casting Information provided by Abatron, Inc. Adheres to metal, glass, ceramics, wood, masonry, etc. Material properties are based on a 2/1 mix ratio. Resin is white, curing agent is black. Gray blend a.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Adell ZS-10 Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Adell ZS-30 Nylon/Olefin Alloy Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | XY; ASTM D638 |
ALM PA 614-GS Filled Nylon 12 Prototyping Polymer 40% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.Drop-in replacement for other commercially .. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ISO 527B |
Ineos Nova 201 Crystal Polystyrene High Heat Extrusion Grade
(discontinued **) Excellent heat resistance, Superior melt strengthApplications: Foam insulation, Oriented polystyrene sheet (OPS), XPS food packaging, Sheet and profile extrusionProperties were determined on injecti.. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | 5 mm/min; parallel to flow; ASTM D638 |
Asahi Kasei Tenac®-C EF750 Acetal Copolymer, Antistat
(discontinued **) Antistatic grade containing special carbon black.Applications: Parts requiring antistatic properties.This product is not a part of the standard product line dated 2003. |
|||
Tensile Strength, Ultimate | 51.0 MPa | 7400 psi | ASTM D638 |
Plenco 2311 Phenolic, Granular, Transfer Molded PLENCO 02311 is a versatile general purpose organic filled phenolic molding compound offering excellent mold processability and optimized cure cycles. PLENCO 02311 is also granulated to provide impr.. |