Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Rotuba H5 Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 52.0 MPa @Temperature 60.0 °C |
7540 psi @Temperature 140 °F |
ISO 527 |
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
PolyOne Stat-Tech™ AS-15GF/000 SD ABS - 15% Glass Fiber Reinforced - Antistatic Protection
(discontinued **)& Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 5000 Black General Purpose Woodflour Filled Phenolic Molding Compound
(discontinued **) Plaslok 5000 is the replacement material for the former Union Carbide BMM-5000. It is a two-stage, woodflour-filled phenolic molding compound having versatile molding performance and preheating cha.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
PolyOne Lubri-Tech™ NL-000/40T Nylon 6/12 - 40% PTFE
(discontinued **) Data provided by PolyOne. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Ineos Styrenics Polystyrene 168M (NAFTA) High heat, high molecular weight general purpose polystyrene with low crystal clarity. It offers high stiffness for extrusion/thermoforming applications, especially for the food packaging.Informati.. |
|||
Tensile Strength, Ultimate | 52.0 MPa @Temperature 23.0 °C |
7540 psi @Temperature 73.4 °F |
ASTM D638 |
IRPC Polimaxx Porene GA850 Acrylonitrile Butadiene Styrene Applications:injection moldinghousing of electrical appliances such as electric fans, telephones, calculators and toys |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | |
Ineos Styrenics Polystyrene 168M0 (NAFTA) High heat, high molecular weight general purpose polystyrene with low residual volatiles. It is ideally suited for use in critical low taste, low odor food packaging products.Information provided b.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | Type 1, 2"/min; ASTM D638 |
Stratasys® Polycarbonate A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating strong parts .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | Type 1, 2"/min; ASTM D638 |
Stratasys® Polycarbonate-ISO PC-ISO (polycarbonate-ISO), an industrial thermoplastic, in its raw state meets the ISO 10993-1 and USP Class VI classification1 and comes in a variety of colors. Because of their strength and medic.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Sumitomo Bakelite Durez® 156 Phenolic, Injection Grade Durez 156 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits excellent dimensional stability, high heat resistance, good molded appearance, and UL.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Sumitomo Bakelite Durez® 22257 Phenolic, Compression Grade Durez 22257 Black Phenolic is a two-stage, asbestos-free, medium impact molding material. It is designed for appliance and electrical applications where additional mechanical strength is required. .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 1508 Polyester, Briquette, Injection Molded PLENCO 01508 is a mineral filled pelletized polyester molding compound, which offers excellent heat resistance and electrical properties. UL recognized under component file E40654. 01508 is availabl.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 2308 Phenolic, Granular, Compression Molded PLENCO 02308 is a general purpose organic filled phenolic molding compound, offering improved heat resistance and optimized cure properties. UL recognized under component file E40654. 02308 is avai.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 7100 Phenolic, Nodular, Injection Molded PLENCO 07100 is an organic fiber reinforced phenolic molding compound, with improved mechanical strength properties and an industrial finish. 07100 is densified for easy handling and good pourabilit.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 7500 Phenolic, Granular, Transfer Molded PLENCO 07500 is an organic reinforced phenolic molding compound, offering improved mechanical strength and excellent cosmetic characteristics. Type ASTM 5948 CFG and UL recognized under component fi.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO 527-1, 2 |
Polyplastics Duranex® 209A Polybutylene Terephthalate (PBT), Low friction, Low wear DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 3597 Phenolic, Granular, Injection Molded PLENCO 03597 is a mineral filled phenolic molding compound offering excellent flammability ratings even at thin cross sections, along with excellent arc and comparative track resistance values. UL r.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 4304 Phenolic, Nodular, Injection Molded PLENCO 04304 is a heat resistant, mineral filled phenolic molding compound offering improved mechanical strength properties along with excellent dimensional stability. UL recognized under component .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plenco 4504 Phenolic, Granular, Injection Molded Plenco 04504 is a renumber of Plaslok 504. Plenco 04504 is a two-stage, mineral and cellulose-filled phenolic molding compound having better impact and heat resistance than general purpose molding c.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | DIN 53504 |
Lubrizol ESTANE® 58563 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO R527 |
Arkema Group Orgalloy® LE 60XV Polyamide 6 Alloy Polyamide Alloy, Semi-Flexible grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | Static |
Channel Industries 300 Barium Titanate Piezoelectric Modified barium titanates are widely used in transducers requiring moderate power level and receiving sensitivity. Special characteristics have made barium titanate a proven material for use in devi.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
Tensile Strength, Ultimate | 52.0 MPa @Thickness 2.00 mm |
7540 psi @Thickness 0.0787 in |
molded plaque, cured 20 hr at 100°C; ASTM D412 |
BASF Elastollan® 1185A10X Wire & Cable Grade Polyurethane Elastomer Compliant with NSF Standard 61 (Drinking water contact). As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO 527-1, 2 |
Polyplastics Duracon® NW-02 Acetal Co-polymer (POM), High sliding, Special lubricant, High sliding DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plaslok 5000 Black General Purpose Woodflour Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use. Plaslok 5000 is the replacement material for .. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
Plaslok 304 Black Impact Grade Woodflour/Cellulose Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 304 is a two-stage, woodflour and cel.. |
|||
Tensile Strength, Ultimate | 52.0 - 125 MPa @Temperature 0.000 - 160 °C |
7540 - 18100 psi @Temperature 32.0 - 320 °F |
Average value: 78.5 MPa Grade Count:2 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |
|||
Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO 527 |
Lubrizol Estane® GP 52 DT Thermoplastic Polyurethane Type: Estane® GP 52DT is an aromatic polyester-based thermoplastic polyurethane (TPU).Features: Translucent spherical pellets.Uses: Injection molding parts, animal identification tagsAvailable in E.. |