Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	765 MPa	111000 psi	Outokumpu Typical, Cold Rolled Strip/Sheet; EN 10002-1
Outokumpu 4318 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled strip/sheet (CPP) and cold rolled strip sheet forms.
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes HastelloyÂ® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095Â°C, and good carburization resistance. Applications includ..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes MultimetÂ® alloy, 25.4-50.8 mm forged bar, 1185Â°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Ultimate	765 MPa @Temperature 315 Â°C	111000 psi @Temperature 599 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes HastelloyÂ® C-22Â® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	765 MPa	111000 psi
Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..