Polymer Property : Tensile Strength, Ultimate = 827 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 827 MPa
120000 psi
Pacific Sintered Materials FX-232-T(HT) Infiltrated High Carbon Steel Powdered Metal
Good strength, shock resistance and hardenability. Moderate tolerance control.Equivalent MPIF Specification: FX-1008-110HTAll information provided by Pacific Sintered Metals.
Tensile Strength, Ultimate 827 MPa
120000 psi
PSM Industries Pacific Sintered Metals Infiltrated High Carbon Steel FX-232-T(HT) Powdered Metal
Good strength, shock resistance and hardenability, Moderate tolerance control Equivalent MPIF Specification: FX-1008-110HTInformation Provided by Pacific Sintered Metals, a division of PSM Industri..
Tensile Strength, Ultimate >= 827 MPa
>= 120000 psi
PSM Industries PolyAlloys WNF-3515 Tungsten Heavy Alloy
Mil. T-21014 Class 3, SAE-AMS-T-21014 Class 3, ASTM-B-777-87 Class 3Information Provided by PolyAlloys, a division of PSM Industries
Tensile Strength, Ultimate >= 827 MPa
>= 120000 psi
PSM Industries PolyAlloys WNF-7129 Tungsten Heavy Alloy
Mil. T-21014 Class 1, SAE-AMS-T-21014 Class 1, AMS 7725 B, ASTM-B-777-87 Class 1Information Provided by PolyAlloys, a division of PSM Industries
Tensile Strength, Ultimate 827 MPa
120000 psi
Hogen Diemitechâ„¢ Tungsten-Based Metal
Diemitech is a new tungsten-based material used for high temperature tooling, die casting, extrusion dies, hot upsetting, and electro brazing. It has a higher tungsten content than similar available..
Tensile Strength, Ultimate 827 MPa
120000 psi
Hogen HM1100 Tungsten-Based Metal
Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers hig..
Tensile Strength, Ultimate 827 MPa
120000 psi
Hogen HM3050 Tungsten-Based Metal
Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; AMS T-21014 Class 3. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers high thermal conductivity and a low CTE..
Tensile Strength, Ultimate 827 MPa
120000 psi
FloMet 17-4 PH Stainless Steel, As Sintered
FloMet provides precision miniature components through metal injection molding (MIM). Metal powders are mixed with thermoplastic binders to form a homogeneous mixture, with approximately 60% volume..
Tensile Strength, Ultimate 827 MPa
120000 psi
Mi-Tech Metals Diemitechâ„¢ Tungsten-Based Metal
Diemitech is a new tungsten-based material used for high temperature tooling, die casting, extrusion dies, hot upsetting, and electro brazing. It has a higher tungsten content than similar available..
Tensile Strength, Ultimate 827 MPa
120000 psi
Mi-Tech Metals HD17D Tungsten-Based Metal
Mil Spec T-21014D Class 1; ASTM B-777-99 Class 1; ASTM B-777-07 Class 1; SAE Aero Material Spec (AMS) 7725C; AMS T-21014 Class 1. Slightly Magnetic.Manufactured by powder metallurgy methods. The t..
Tensile Strength, Ultimate 827 MPa
120000 psi
Mi-Tech Metals HD18D Tungsten-Based Metal
Mil Spec T-21014D Class 3; ASTM B-777-99 Class 3; ASTM B-777-07 Class 3; AMS T-21014 Class 3. Slightly Magnetic.Manufactured by powder metallurgy methods. The tungsten base offers high thermal con..
Tensile Strength, Ultimate 827 MPa
120000 psi
621°C Temper Temperature
Latrobe Lescalloy® 16NCD13 VAC-ARC High Strength Alloy Steel
16NCD13 VAC-ARC is a premium quality low alloy, carburizing casehardenable vacuum arc remelted steel which takes its name from the French industry designation. In the carburized condition, its high ..
Tensile Strength, Ultimate 827 MPa

@Temperature 427 °C
120000 psi

@Temperature 801 °F
Haynes Ultimet® alloy, 1.6 mm sheet
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Ultimate 827 MPa
120000 psi
Special Metals Electroformed Nickel, 6 Micron (0.24 mil) Foil, As-Electroformed
Data provided by the manufacturer, Special Metals.
Tensile Strength, Ultimate 827 MPa
120000 psi
Annealed
Universal Wire Works 5Al-2.5Sn (AMS 4953) Titanium Alloy Filler Metal
Universal Ti 5Al-2.5Sn titanium alloy is easily joined with the gas tungsten arc, gas metal arc or resistance welding processes. 100% joint efficiency can be obtained provided proper shielding proce..
Tensile Strength, Ultimate 827 MPa
120000 psi
CMW® ELKON 100W Pure Tungsten
Tungsten, also called Wolfram, occurs as an impure tungsten oxide in wolframite and sche ores. It is chemically extracted, refined to an oxide of high purity and reduced to tungsten powder in hydrog..
Tensile Strength, Ultimate >= 827 MPa
>= 120000 psi
Mid-radius
Dura-Bar 120-90-02 Continuously Cast Ductile Iron Bar Stock ASTM A536
Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for..
Tensile Strength, Ultimate 827 MPa
120000 psi
cold worked
CMW® ELKONIUM 301 platinum based alloy
Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (..
Tensile Strength, Ultimate 827 MPa
120000 psi
cold worked
CMW® ELKONIUM 306 platinum based alloy
Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (..
Tensile Strength, Ultimate 827 MPa
120000 psi
CMW® THERMKON® 68 Tungsten Copper parts
For matching CTE of semiconductor substrates while allowing high thermal transfer.Information provided by CMW Inc.
Tensile Strength, Ultimate 827 MPa

@Temperature -129 °C
120000 psi

@Temperature -200 °F
Longitudinal
Carpenter 20Cb-3® Stainless Steel
Data provided by Carpenter Technology Corporation.20Cb-3® is an austenitic stainless steel possessing excellent resistance to hot sulfuric acid and many other aggressive environments which would re..
Tensile Strength, Ultimate 827 - 965 MPa
120000 - 140000 psi
Ametek AM 388™ Alloy (UNS C72650) TM06
Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and..
Tensile Strength, Ultimate 827 - 965 MPa
120000 - 140000 psi
Ametek AM 388™ Alloy (UNS C72650) TX00
Information supplied by Ametek Specialty Metal Products Division.Copper base Spinodal alloy with high conductivity and high strength. Outstanding performance for contacts in connectors, sockets and..
Tensile Strength, Ultimate 827 MPa
120000 psi
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 10% Cold Work
Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..
Tensile Strength, Ultimate 827 MPa
120000 psi
Solution Annealed
ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy
Characteristics: high strength up to 1500°F, oxidation resistance up to 2000°FInformation provided by Allegheny Ludlum
Tensile Strength, Ultimate 827 MPa
120000 psi
Beta Quenched
ATI Wah Chang Tiadyne™ 3510
Capable of being surface hardened to depths that produce very high wear resistance. Produced by traditional metallurgical processing, not special treatments.Information provided by ATI Wah Chang
Tensile Strength, Ultimate 827 MPa
120000 psi
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Tensile Strength, Ultimate 827 MPa
120000 psi
Carpenter Hiperco® 50 Fe-Co-V Soft Magnetic Alloy, 0.15 mm Strip Heat Treated 760°C
Hiperco® alloy 50 is an iron-cobalt-vanadium soft magnetic alloy which exhibits high magnetic saturation (24 kilogauss), high D.C. maximum permeability, low D.C. coercive force, and low A.C. core l..
Tensile Strength, Ultimate >= 827 MPa
>= 120000 psi
PSM Industries PolyAlloys WNF-5421 Tungsten Heavy Alloy
Mil. T-21014 Class 2, SAE-AMS-T-21014 Class 2, ASTM-B-777-87 Class 2Information Provided by PolyAlloys, a division of PSM Industries
Tensile Strength, Ultimate 827 MPa
120000 psi
Special Metals INCOLOY® 27-7MO Super-Austenitic Stainless Steel
INCOLOY® alloy 27-7MO (UNS S31277; EP 1,263,999 B1) is an advanced 7% molybdenum super-austenitic stainless steel offering corrosion resistance in most environments superior to 6% molybdenum super-..