Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cookson Group Plaskon® 3300SGH Mineral Filled Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Exhibits exceptional reliability, excellent moldability, good release characteristics, low flash and rapid cure. This compound i.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
IDI Composites C-108 Thermoset Polyester, Molding Vinylester compounds in a range of strengths with superior corrosion resistance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, DAM Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by G.. |
|||
Tensile Strength, Ultimate | 83.0 MPa @Temperature 1095 °C |
12000 psi @Temperature 2003 °F |
|
Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Haysite 46000 Polyester SMC, 30% Glass Reinforced The 46000 series sheet molding compound is designed for "automotive type" applications requiring good mechanical properties and low shrink characteristics. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN138R Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Sumitomo Bakelite North America RX® 3-1-525F-P Short-Glass Reinforced Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SDG-F.I.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Sumitomo Bakelite Sumikon® PM-9501 Glass-Filled Phenolic, Compression Grade Sumikon PM-9501 is a two stage glass fiber and mineral filled black phenolic special purpose molding compound. It is especially designed for applications requiring high strength and dimensional s.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Plenco 1530 Polyester, Briquette, Transfer Molded PLENCO 01530 is a glass and mineral reinforced pelletized polyester molding compound, offering improved mechanical strength properties along with excellent electrical properties and dimensional stab.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E486 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E487 lass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cosmic Plastics E4920 Mineral Filled Epoxy Molding Compound, Encapsulated Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 520S-13GU Nylon 66, 13% Glass Reinforced Nylon 66, 13% Glass reinforced resin with heat stabilizer, utility grade. Also available in black (520S-13GBU).Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® N541L Nylon 66 A general purpose injection molding grade for heavy parts.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® P1525B Polycarbonate A rigid flame retardant black polycarbonate, for applications requiring superior dimensional stability and overall toughness.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | Static |
Channel Industries 5800 Lead Zirconate Titanate Piezoelectric Characterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most extensively used .. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Chem Polymer Chemlon 100 X Nylon 66, Lubricated GP A medium viscosity, general purpose injection molding grade nylon 66. Internally and externally lubricated for excellent feed and mold release properties.Data provided by the manufacturer, Chem Pol.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 431 Glass Reinforced, PBT Alloy Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 511 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.10% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 1420B Polycarbonate, 20% Glass Reinforced A 20% glass reinforced polycarbonate for increased mechanical strength and thermal properties, modified for good impact with increased dimensional stability and overall toughness. 1423B with UV sta.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 830L Nylon 6 Basic Nylon 6, medium viscosity, lubricated.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 830LB Nylon 6 Basic Nylon 6, medium viscosity, lubricated black.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | Static |
Channel Industries 5804 Lead Zirconate Titanate Piezoelectric Navy Type IIICharacterized by high coupling factors and high piezoelectric and dielectric constants over extended temperature ranges and stress amplitudes, lead zirconate titanates are the most exte.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ATSM D638 |
Ashley Polymers Ashlene® 830LW Nylon 6 Basic Nylon 6, medium viscosity, lubricated for general purpose injection molding.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
Sumitomo Bakelite Sumikon® PM-6430 Glass-Filled Phenolic, Compression Grade Sumikon PM-6430 black Phenolic is a two stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional sta.. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
Cookson Group Plaskon® 3300S Mineral Filled Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low stress, flame retardant, novolac hardened epoxy molding compound designed to provide hermeticity protection exceeding that .. |
|||
Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | DIN 53455; ASTM D638 |
Kolon Kopa® KN173MT40 Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |