Polymer Property : Tensile Strength, Ultimate = 830 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	830 MPa @Temperature -80.0 °C	120000 psi @Temperature -112 °F	EN min; EN 10002-5
Outokumpu 4307 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Tensile Strength, Ultimate	830 MPa	120000 psi	Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Outokumpu SAF 2507® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone..
Tensile Strength, Ultimate	830 MPa	120000 psi
Polyimide Fiber
Tensile Strength, Ultimate	830 MPa	120000 psi
Haynes HastelloyÂ® W alloy, gas tungsten arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Ultimate	830 MPa	120000 psi	Plate
Haynes 282Â® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNESÂ® 282Â® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Tensile Strength, Ultimate	830 MPa	120000 psi
Haynes 556Â® alloy, bar, after 1000 hours at 650Â°C (1200Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	830 MPa @Temperature 95.0 Â°C	120000 psi @Temperature 203 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	830 MPa	120000 psi
ATI Allegheny Ludlum AL 17-7™ High Strength Stainless Steel, UNS S17700 Property data below is typical of annealed samples. Available in sheet and strip. For use in high-strength springs, bellows, and aerospace applications.Information provided by Allegheny Ludlum
Tensile Strength, Ultimate	830 MPa	120000 psi
Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..