- Polymer Property : Tensile Strength, Ultimate = 860 MPa
Polymer Property : Tensile Strength, Ultimate = 860 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 860 MPa @Temperature -80.0 °C |
125000 psi @Temperature -112 °F |
EN min; EN 10002-5 |
| Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
| Tensile Strength, Ultimate | >= 860 MPa | >= 125000 psi | |
| MetalTek IN® 718 UNS N07718 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | >= 860 MPa | >= 125000 psi | |
| MetalTek MTEK 718 Cast UNS N07718 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
| Tensile Strength, Ultimate | >= 860 MPa | >= 125000 psi | |
| MetalTek RENE® 77 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTekWrought Grade RENE® 77 |
|||
| Tensile Strength, Ultimate | 860 MPa @Temperature 705 °C |
125000 psi @Temperature 1300 °F |
|
| Haynes 242® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes Hastelloy® alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Tensile Strength, Ultimate | >= 860 MPa | >= 125000 psi | Longitudinal |
| TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; Medium To High Strength General-Purpose Alloy. Minimum tensile property data below are specific to this MatWeb entry; other specific form/thickness entries are also available in MatWeb.Features: A.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Elgiloy® Co-Cr-Ni Alloy, Strip General Elgiloy® information: High strength, ductility, fatigue life, and good mechanical properties. Corrosion resistant in numerous environments. Available in strip (currently 0.0015" to 0.075".. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Elgiloy® Co-Cr-Ni Alloy, Strip, Heat Treated Heat Treatment 5 hours at 482°C. The strength and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, duc.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Ametek 17-4 P/M Process, Sintered at 2200°F (1204°C) Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treat.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| ATI Allvac® REX 734™ UNS S31675 Specialty Steel Uses: Medical and surgical devices; forged mono-block hip stems.Property values are for samples in the metallurgical condition: As rolled, warm worked.Information provided by Allvac, An Allegheny Te.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | Typical; Annealed |
| ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Sheet and Strip < 0.1875", UNS S31803 Ferromagnetic. The AL 2205 alloy is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly improved the corrosion resistance of the alloy; especially in the welded c.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||