Polymer Property : Tensile Strength, Ultimate = 865 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	865 MPa @Temperature 540 Â°C	125000 psi @Temperature 1000 Â°F
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	865 MPa	125000 psi
Haynes 556Â® alloy, 30% cold reduction, 1065Â°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	865 MPa	125000 psi
Haynes 556Â® alloy, bar, after 8000 hours at 760Â°C (1400Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	865 MPa	125000 psi
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Tensile Strength, Ultimate	865 MPa @Temperature 760 °C	125000 psi @Temperature 1400 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..