Polymer Property : Tensile Strength, Ultimate = 870 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 870 MPa
126000 psi
Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F)
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate 870 MPa
126000 psi
Haynes Hastelloy® W alloy, gas metal arc welds, as-welded
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Ultimate 870 - 1030 MPa

@Diameter 9.52 mm
126000 - 149000 psi

@Diameter 0.375 in
CWSR; DAN 2700.9
Haynes Ti-3Al-2.5V Alloy Titanium Tubing
Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani..
Tensile Strength, Ultimate 870 - 1030 MPa

@Diameter 12.7 - 25.4 mm
126000 - 149000 psi

@Diameter 0.500 - 1.00 in
CWSR; DAN 2700.9
Haynes Ti-3Al-2.5V Alloy Titanium Tubing
Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani..
Tensile Strength, Ultimate 870 MPa
126000 psi
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate 870 - 970 MPa
126000 - 141000 psi
CLAL-MSX NICLAFOR® 1000 TH1 Quenched/Precipitation Heat Treated, Drawn Copper Alloy
Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate 870 MPa
126000 psi
R<sub>m</sub>, @RT, 270 HB.
Assab Steels CARMO Cold Work Steel
CARMO is a high-strength, flame-induction and through hardening steel delivered prehardened to 240-270 HB.The surface of the steel can be flame-hardened without water cooling to a hardness of 58±2..