Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 4.83 MPa | 700 psi | Tensile Shear Strength; ASTM D1002 |
Protective Coating PC-Fahrenheit™ High Temperature Epoxy PC-Fahrenheit™ is a hand moldable putty epoxy designed for quick emergency-type repairs formulated for increased temperatures. PC-Fahrenheit™ can be expected to outperform other putties at high te.. |
|||
Shear Strength | >= 4.83 MPa | >= 700 psi | |
Parker Chomerics CHO-BOND 584-208 Conductive Adhesive Two-component, highly conductive adhesive system that combines the good adhesive characteristics of epoxy with the superior conductivity of silver. In addition to being available in bulk form, the m.. |
|||
Shear Strength | 4.83 - 46.9 MPa | 700 - 6800 psi | Average value: 20.1 MPa Grade Count:23 |
Overview of materials for Epoxy, High Temperature This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Mineral Filled". Each property range of values reported is minimum and maximum val.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® CR III 1/4-5052-.004 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® HRH-327 - 3/16 - 8.0 Fiberglass Reinforced Polyimide Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well a.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® HRP - 3/8 - 8.0 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Plate Shear, L Direction, typ |
Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.004 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | 4.83 MPa | 700 psi | On Douglas Fir |
3M Scotch-Weld™ 3779 Hot Melt Adhesive High heat resistance; High strength; Good fuel and oil resistance and ElectronicsInformation provided by 3M |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Rigid PVC; ASTM D1002-64 |
3M Scotch-Weld™ CA100 Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. High-peel and impact strength and high thermal shock and heat resistance.Information provided by 3M.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Wood, Fir |
3M Scotch-Weld™ DP100 Plus Clear Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is a unique among fast setting mercaptan cure epoxies in that it comb.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Abraded Aluminum, 3 days, 71°C, 100% RH |
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 4.83 MPa @Temperature 49.0 °C |
700 psi @Temperature 120 °F |
Overlap |
3M Scotch-Weld™ DP125 Gray Epoxy Adhesive Scotch-Weld epoxy adhesive DP125 Gray is a filled, pigmented version of the Scotch-Weld epoxy adhesive DP125 Translucent and has similar performance and flexibility properties.Information provided b.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, ABS |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Shear Strength | 4.83 MPa @Time 1800 sec |
700 psi @Time 0.500 hour |
Aluminum Overlap |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 4.83 MPa @Temperature 82.0 °C, Time 900 sec |
700 psi @Temperature 180 °F, Time 0.250 hour |
Aluminum, Overlap |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, ABS, Adhesive/Cohesive Failure |
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Polycarbonate, Adhesive/Cohesive Failure |
3M Scotch-Weld™ DP8810NS Low Odor Acrylic Adhesives 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are high performance, two-part acrylic adhesives with lower odor than most acrylic adhesives. These toughened products offer excellent shear, peel, and .. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Pine, Substrate/Cohesive Failure |
3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 4.83 MPa @Temperature 66.0 °C |
700 psi @Temperature 151 °F |
Overlap, Plywood, Substrate Failure |
3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Fir, 50% RH |
3M 5200 Marine Adhesive/Sealant 3M™ Marine Adhesive/Sealant 5200 is a one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds. It has excellent adhesion to wood, gelcoat and fiberglass. It for.. |
|||
Shear Strength | 4.83 MPa @Temperature 49.0 °C |
700 psi @Temperature 120 °F |
Overlap, HDPE, Cohesive Failure |
3M Scotch-Weld™ DP8005 Translucent Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl.. |
|||
Shear Strength | 4.83 MPa @Temperature 49.0 °C |
700 psi @Temperature 120 °F |
Overlap, Green FRP, Cohesive Failure |
3M Scotch-Weld™ DP8005 Translucent Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl.. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Fiberglass Reinforced Plastic |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Abraded Aluminum, 3 days, 71°C, 100% RH |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Wood, Fir |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |
|||
Shear Strength | 4.83 MPa | 700 psi | Overlap, Polycarbonate |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |