Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 50.0 - 65.0 MPa | 7250 - 9430 psi | Average value: 58.0 MPa Grade Count:3 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Shear Strength | 50.0 - 76.5 MPa | 7250 - 11100 psi | Average value: 61.7 MPa Grade Count:5 |
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr.. |
|||
Shear Strength | 50.0 - 90.0 MPa | 7250 - 13100 psi | Average value: 76.8 MPa Grade Count:26 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Shear Strength | 50.0 MPa | 7250 psi | 0º, Short Beam |
Hexcel® HexPly® M34 75°C (167°F) Curing Epoxy Matrix, E-glass Balanced Fabric 300 g/m2 Information provided by HexCel |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. Impact-resistant. Resistant to mechanical wear and noise-reducing. The graphite content causes low friction. Well suited for parts where there a.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola Etronax MMF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Reinforced with a finer cotton fabric than Etronax MF. Also well suited in particular for small components which are subject to mechanical load and wear. Can be machined to finer tolera.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola Etronax MMMF Phenolic, Cotton Fabric Reinforcement, Light Brown, Sheets Description: Friction reducing material consisting of phenolic resin and a very fine cotton fabric. Exclusively for mechanical applications. Good dry-run properties but can be lubricated with oil, g.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Sheet High performance/price ratio insulation material. Self-extinguishing, halogen-free, very low smoke emission and toxicity. Mechanically much stronger than the Etronit and Etronax types.Information pr.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola G-Etronax EP 10 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets Description: High mechanical strength at elevated temperatures. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. Can be used at c.. |
|||
Shear Strength | 50.0 MPa @Thickness >=5.00 mm |
7250 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
Elektro-Isola G-Etronax EP 203 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets Description: High mechanical strength at elevated temperatures. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. Can be used at c.. |
|||
Shear Strength | 50.0 - 65.0 MPa | 7250 - 9430 psi | IS 867-1963 |
Amity Thermosets ATE 183 M Phenolic Molding Mica and organic Filler, Compression Molded Characteristics:Electric low loss Low water absorption Low shrinkage Heat stableGlossy surface finishVery good mouldabilityGood electrical insulationGood chemical resistantColor-blackMedium flowAppl.. |
|||
Shear Strength | 50.0 - 65.0 MPa | 7250 - 9430 psi | IS 867-1963 |
Amity Thermosets ATE 183 Phenolic Molding Mica and organic Filler, Compression Molded Characteristics:Electric low loss Low water absorption Low shrinkage Heat stableGlossy surface finishVery good mouldabilityGood electrical insulationGood chemical resistantColor-blackMedium flowAppl.. |