Polymer Property : Tensile Creep Modulus, 1000 hours = 102000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Creep Modulus, 1000 hours 700 - 1800 MPa
102000 - 261000 psi
Average value: 1260 MPa Grade Count:20
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim..
Tensile Creep Modulus, 1000 hours 700 - 1600 MPa
102000 - 232000 psi
Average value: 1280 MPa Grade Count:9
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an..
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
Average value: 700 MPa Grade Count:3
Overview of materials for Nylon 66, Unreinforced, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum ..
Tensile Creep Modulus, 1000 hours 700 - 8300 MPa
102000 - 1.20e+6 psi
Average value: 3230 MPa Grade Count:3
Overview of materials for Nylon, Amorphous Transparent Alloy
This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value..
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
Lanxess Durethan® A 30 H2.0 901510 Nylon 66
PA 66 standard injection molding grade, non-reinforced, very easy release, good heat-ageing resistanceApplication Examples: terminal blocks, cable clips, bobbins, gearwheels
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
Lanxess Durethan® B 31 SK 000000 Nylon 6
PA 6, injection molding grade, non-reinforced, easy flow, easy-release, rapid solidification, crystallizes somewhat more finely and uniformly than B 30 S
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
Lanxess Pocan® S 1506 000000 PBT
PBT, non-reinforced, injection molding extrusion, impact modified
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
Lanxess Durethan® A 30 000000 Nylon 66
PA 66, standard injection molding grade, non-reinforced, very easy release, normal solidificationApplication Examples: terminal blocks, cable clips, bobbins, gearwheels
Tensile Creep Modulus, 1000 hours 700 MPa

@Temperature 23.0 °C
102000 psi

@Temperature 73.4 °F
50%RH; ISO 899
DuPont Performance Polymers Zytel® ST801A NC010A Nylon 66  (Unverified Data**)
Zytel® ST801A NC010A is a Super Tough, high performance, polyamide 66 resin. It is partially UV stabilized and when appropriately colored offers limited protection to indirect sunlight exposure.Inf..
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899
BASF Ultramid® A34 01 PA66 (Conditioned)
Ultramid A34 01 is an intermediate visosity, PA66 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or ..
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899
BASF Ultramid® B3K PA6 (Conditioned)
Ultramid B 3K is an easy flowing, stabilized for fast processing, grade of nylon 6.
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
BASF Ultraform® N2650 Z2 (LEV) POM
Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information pr..
Tensile Creep Modulus, 1000 hours 700 MPa
102000 psi
ISO 899-1
BASF Ultramid® A3K BK 00464 PA66 (Conditioned)
Description: Easy flowing injection-molding grade for fast processing. Uses include highly stressed technical parts such as bearings and gear wheels; also electrically insulating parts such as termi..
Tensile Creep Modulus, 1000 hours 700 MPa

@Strain <=0.500 %
102000 psi

@Strain <=0.500 %
ISO 899-1
BASF Ultramid® A4H PA66 (Dry)
Description: Highly heat aging resistant, medium-viscosity injection-molding grade for highly stressed parts such as bearing cages, gearwheels, spool bodies and chain drive tensioners.Information pr..
Tensile Creep Modulus, 1000 hours 700 MPa

@Strain <=0.500 %
102000 psi

@Strain <=0.500 %
ISO 899-1
BASF Ultramid® B3K BK00464 PA6 (Conditioned)
Description: Easy flowing and stabilized injection-molding grade used for technical parts with wall thicknesses >2 mm, e.g. machinery components, fans and power tool housings.Information provided by..
Tensile Creep Modulus, 1000 hours 700 MPa

@Time 3.60e+6 sec
102000 psi

@Time 1000 hour
50%RH; ISO 899-1
DuPont Performance Polymers Zytel® 101 NC010 Nylon 66  (Unverified Data**)
Unreinforced Polyamide 66Zytel 101 NC010 is a general purpose polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers