Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1000 hours | 3000 - 7000 MPa | 435000 - 1.02e+6 psi | Average value: 5030 MPa Grade Count:3 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant". Each property range of values re.. |
|||
Tensile Creep Modulus, 1000 hours | 3000 MPa | 435000 psi | ISO 899 |
BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Conditioned) Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. |
|||
Tensile Creep Modulus, 1000 hours | 3000 MPa @Strain <=0.500 % |
435000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® B3ZG6 BK 30564 30% Glass Filled PA6-1 (Conditioned) Description: Impact-modified and 30% glass fiber reinforced injection-molding grade for technical articles of very high stiffness and toughness, for instance, for vehicle airbag housings and suitcas.. |
|||
Tensile Creep Modulus, 1000 hours | 3000 MPa @Strain <=0.500 % |
435000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating partsInformation provided by BASF |
|||
Tensile Creep Modulus, 1000 hours | 3000 MPa @Strain <=0.500 % |
435000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
Tensile Creep Modulus, 1000 hours | 3000 MPa @Strain <=0.500 % |
435000 psi @Strain <=0.500 % |
ISO 899-1 |
BASF Ultramid® B3WG5 BK 00564 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |