- Polymer Property : Flexural Modulus = 1.45 GPa
Polymer Property : Flexural Modulus = 1.45 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 1.45 GPa | 210 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Multibase Nylex™ 2185 HF Black Polyamide + PP Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | |
| Plastcom SLOVALEN PC 63 T 15 PP reinforced with 15% mineral filler Features: Modified PP for injection moulding with the content of 15% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. Application in all automotive interior industry.D.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| PolyOne Maxxam™ PPC-20C Nat Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Network Polymers NPP 30-007W Description: Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | |
| Plastcom SLOVAMID 6 T 30 TS PA6, 30% mineral filling FeaturesDecreased shrinkage against the BT types, increased heat application. Increased modulus in tension - strength of the material. PA matrix reduction. PA for injection moulding with the content.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Polimeri Europa Eraclene® MP 90 High Density Polyethylene - Injection Molding Eraclene MP 90 is a high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MP 90 has a narrow molecular weight distribution and a h.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | 2 mm/min; ISO 178 |
| Inno-Comp INNOPOL® CS 2-3522 TO BU 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-3522 TO BU is a 20% talc-filled, elastomer modified, UV-stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3522 TO BU is developed for producing injection m.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Iran Petrochemical (PCC) S 30 S Polypropylene This grade is for general injection molding applications.Applications: textile bobbins ,wheels ,fittings ,closures ,caps.Information provided by Iran Petrochemical Commercial Co. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Iran Petrochemical (PCC) T 30 S Polypropylene T30S is a polypropylene homopolymer particularly suitable for the extrusion of sheet for thermoforming, film yarn and mono filament.Applications: T30S is designed for bags industrial fabrics and mat.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | 1% Secant; ASTM D790 |
| IRPC Polimaxx Polene 2300NCA Polypropylene Block Copolymer CHARACTERISTICS: HIGH STIFFNESS, HIGH IMPACT, MEDIUM FLOW, HEAT STABILITY CONTAIN UV STABILIZER ADDITIVE APPLICATIONS: INJECTION MOLDING SPECIALLY FOR BATTERY CASES, AUTOPARTS AND ELECTRICAL APPLIAN.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | 2mm/min; ISO 178 |
| Borealis HK030U Polypropylene Compound HK030U is a special low viscosity polypropylene compound developed to fit the production of PP-GF composites in the direct LFT compression and injection molding process as well as in combination wit.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene DescriptionPolypropylene PP 1255-01 Natural is a general purpose molding grade, with UL 94 HB approval, homopolymer polypropylene. ApplicationPolypropylene PP 1255-01 meets FDA Regulation 21 CFR 177.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Chase Plastics CP Pryme® NNA100 (Dry) ABS Polyamide Alloy Features: Good abrasion resistancePleasing surface appearanceGood chemical resistanceHigh impact resistanceHigh rigidityLow shrinkageSolvent resistanceHigh strengthGood thermal stabilityGood toughne.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | 1.3mm per min, 1% secant; ASTM D790 |
| Formosa Plastics Formolene® 5140N Homopolymer Polypropylene Homopolymer for Injection Molded Applications Formolene 5140N is a highly isotactic, polypropylene homopolymer with fast cycle time and improved mold release. It has use in injection molded applicat.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Total PPH 4069 Polypropylene Homopolymer, Fiber Polypropylene PPH 4069 is a homopolymer polypropylene with a Melt Flow index of 4 g/10 min.Polypropylene PPH 4069 is intended for extrusion of high tenacity staple fibers for non-woven applications... |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 527-2 |
| Total PPH 7069 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 7069 is homopolymer.ApplicationATOFINA Polypropylene PPH 7069 is characterized by medium fluidity for extrusion of continuous filament (CF) and bulk continuous filament (BC.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
| Total PS CPDS 9217 Compound Polystyrene/Polyethylene POLYSTYRENE (PS) COMPOUND (CPDS) 9217 is an alloy of polystyrene and polyethylene. This combination brings the benefits of polyethylene; a high level of stress crack resistance, mechanical properti.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene DescriptionPolypropylene PP 1255-01 Natural is a general purpose molding grade, with UL 94 HB approval, homopolymer polypropylene. ApplicationPolypropylene PP 1255-01 meets FDA Regulation 21 CFR 177.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| UBE UBESTA® 3030LUX Rigid Automotive Grade Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat.. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Aaron Industries AAROLENE® ARPP C 200-2 Polypropylene Compounded Resin AAROLENE® ARPP 200 Series Polypropylene Compounded ResinColor may be specified. Melt Flow Index may be specified. |
|||
| Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
| Aclo Accutech Polypropylene HP0315V Homopolymer High Heat Approved to GMP.PP.013 |
|||