Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.05 GPa | 1020 ksi | ISO 178 |
Radici Radilon® SRCP3010LK (dry) Nylon 6 Heat stabilized glass-fiber reinforced and mineral reinforcedInformation provided by Radici group. |
|||
Flexural Modulus | 7.00 - 10.0 GPa | 1020 - 1450 ksi | Injection; ISO 178 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Flexural Modulus | 7.00 GPa @Temperature 23.0 °C |
1020 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANTEC PC S75R GF30 V0 Polycarbonate, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Flexural Modulus | 7.00 - 18.0 GPa | 1020 - 2610 ksi | Average value: 14.3 GPa Grade Count:8 |
Overview of materials for Epoxy Encapsulant, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Encapsulant, Unreinforced". Each property range of values reported is minimum and maximum values o.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
Hexion Bakelite™ PF 7400 Phenolic Formaldehyde Resin, High Mechanical Strength
(discontinued **) Phenolic molding compound, organically filled, reinforced with cotton fiber flakes, high notched impact strength.Application areas: Moldings for higher mechanical strain, e.g. power plugs high volta.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
Hexion Bakelite™ PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Listed
(discontinued **) Phenolic molding compound, mainly organically filled, very soft flow for large molds, UL listed molding compound 1.5 mm/V-1 (BK), 3.0 mm/V-0 (BK).Application areas: Pan handles, various applications.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
Plaslok 307 Black Impact Grade Mineral/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 307 is a two-stage, mineral and flock.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1105-7835 PEEK, with glass fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Low warpage, isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts,.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 1700-8019 PPO, with glass fiber and PTFE, low-warpage Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Improved friction and wear behaviour... |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 3-7234-1 Polyamide 6, with carbon fiber, electrically conducting Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Strong, stiff parts.dynamic stressAntistatic.Handles, levers, rollers, body parts.Information provided by L.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 50-7154/V0 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Lehmann & Voss LUVOCOM® 50-7586 Polycarbonate, with carbon fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts with low warpage and.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | |
Idemitsu Kosan Xarec® WA 210 SPS, 20% Glass Filled Crystalline Polymer, Glass Filled, Impact Modified, Improved Mold Release. Used in Automotive and Industrial applications. |
|||
Flexural Modulus | 7.00 GPa @Temperature 22.0 °C |
1020 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® SMC 0650 Unsaturated Polyester UP SMC 0650 Low pressure SMC for large panels when moulding force becomes critical. Specific moulding pressure < 20 bar. A Special molding procedure is necessary.Information Provided by Menzolit |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | cond., 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 25 F30 000000 Nylon 6, Glass Fiber Reinforced, Flame Retardant PA 6, 25% glass fibers, injection molding, flame retardantInformation provided by LANXESS. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min; ASTM D790 |
Lavergne VYPET VNT 325 PET 25% Glass - Mineral Reinforced Vypet 325 is a 25% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications.Features: High temperature performance; Good balance resilience-stiffne.. |
|||
Flexural Modulus | 7.06 GPa @Thickness 6.40 mm |
1020 ksi @Thickness 0.252 in |
1.3mm/min; ASTM D790 |
LG Chemical LUPOL LW4405 PP+GF/MF40% Description: Injection Molding, PP+GF/MF40%, Low WarpageApplication: Electrical, Electronic and Automotive Parts CAS: 9003-07-0, 65997-17-3 and 12001-26-2Information provided by LG Chemical |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 830F PBT+PET (Europe-Africa-Middle East) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON SE003 PA 12 LNP* STAT-KON* SE003 is a compound based on Nylon 12 resin containing 15% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10 LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 7.05 GPa | 1020 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KE002 ACETAL LNP* STAT-KON* KE002 is a compound based on Acetal resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM-D790 |
Polyram PlusTek PB321I6 Nylon 6, 30% Glass Fiber and Mineral 30% glass fiber and mineral reinforced polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | >= 7.00 GPa | >= 1020 ksi | IEC 1212-2 5.2 |
Hippe PF CC 203 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet Used in mechanical applications (fine weave: =130 g/m2, >30 threads/cm). Recommended for small parts. Better mechanical properties and poorer electrical properties than type PF CC 204.Information .. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
Eurotec® Tecomid® NA40 GR30 NL IH PA 6.6 30% glass fiber reinforced, impact modified Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ISO Data |
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G .. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
Beijing Ranger Chem PBT-201-G20 291 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
Ashley Polymers Ashlene® 528SMS-30GB Nylon 66, 30% Glass Reinforced A 30% glass reinforced, heat stabilized, black Nylon 66 with Molybdenum disulfide.Data provided by the manufacturer |
|||
Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
Sumitomo Bakelite North America FM 3000 Cellulose Reinforced Phenolic Novolac FM 3000 is a self-lubricated cellulose reinforced phenolic molding compound, modified for applications requiring reduced friction and low wear. Information supplied by Sumitomo Bak North America... |