Polymer Property : Flexural Modulus = 1160 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Compression; ISO 178
Raschig Group AMPLA® 2000 melamine-modified polyester
Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection; ISO 178
Raschig Group AMPLA® 2500 melamine-modified polyester
Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Flexural Modulus 7.00 - 8.00 GPa
1020 - 1160 ksi
Injection and Compression; ISO 178
Raschig Group AMPLA® 7250 melamine-modified polyester
Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection and Compression; ISO 178
Raschig Group AMPLA® 7500 melamine-modified polyester
Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection; ISO 178
Raschig Group DECAL® 2061 Phenolic
Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and ..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection and Compression; ISO 178
Raschig Group DECAL® 5431 Phenolic
Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection; ISO 178
Raschig Group MELOPAS® 6605 MP Melamine
Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be..
Flexural Modulus 5.00 - 8.00 GPa
725 - 1160 ksi
Injection and Compression; ISO 178
Raschig Group MELOPLAS® 2500 MF
Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Flexural Modulus 1.29 - 8.00 GPa
186 - 1160 ksi
Average value: 5.61 GPa Grade Count:3
Overview of materials for PCT, 40% Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr..
Flexural Modulus 2.00 - 8.00 GPa
290 - 1160 ksi
Average value: 5.22 GPa Grade Count:112
Overview of materials for Polycarbonate, 20% Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E..
Flexural Modulus 0.800 - 8.00 GPa

@Temperature -40.0 - 120 °C
116 - 1160 ksi

@Temperature -40.0 - 248 °F
Average value: 2.65 GPa Grade Count:4
Overview of materials for Nylon 6, 30% Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are includ..
Flexural Modulus 3.45 - 8.00 GPa
500 - 1160 ksi
Average value: 4.59 GPa Grade Count:12
Overview of materials for Nylon 12, 20% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. ..
Flexural Modulus 6.50 - 8.00 GPa
943 - 1160 ksi
ISO 178
Vyncolit 2530 W Novolac Phenolic
Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
ISO 178
Vyncolit 2723 W Novolac Phenolic
Mineral and organic filled phenolic molding compound with excellent mechanical, thermal and dielectric properties. I2/FO classified under NF F 16-101 (Fire & Smoke classification).USES: Circuit bre..
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
ISO 178
Vyncolit 2920 W Novolac Phenolic
Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B..
Flexural Modulus 5.00 - 8.00 GPa
725 - 1160 ksi
ISO 178
Bulk Molding Compounds tetra-DUR F 4001 Bulk Molding Compound
UL-Licensed, Abrasion resistance, free of fiber glass.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipati..
Flexural Modulus 1.70 - 8.00 GPa

@Temperature -40.0 - 120 °C
247 - 1160 ksi

@Temperature -40.0 - 248 °F
Average value: 3.83 GPa Grade Count:5
Overview of materials for Nylon 6, 20% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea..
Flexural Modulus 1.60 - 8.00 GPa
232 - 1160 ksi
Average value: 5.28 GPa Grade Count:278
Overview of materials for Polypropylene with 30% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..