- Polymer Property : Flexural Modulus = 1240 ksi
Polymer Property : Flexural Modulus = 1240 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 8.54 GPa | 1240 ksi | |
| Plastcom SLOVAMID 6 GF 30 FRGG2 PA6, 30% glass fibre, flame retardant Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | STN EN ISO 178 |
| Plastcom SLOVAMID® 6 GF 30 FRG 2 PA6 reinforced with glass fiber, flame retarded PA 6 for injection molding, reinforced with 30 % glass fiber, flame retarded with halogen free flame retardant. Main features: flammability in accordance with UL 94 5 at 3.2 mm. Application for the .. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| PolyOne Stat-Tech™ PC-15CF/000 Black Polycarbonate (PC) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
| Flexural Modulus | 8.53 GPa @Thickness 3.20 mm |
1240 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID GP2259AFL PA6+GF25%, Flame Retardant Feature: Injection Molding, PA6+GF25%, Flame RetardantApplication: IT/OA (Connector)CAS No. 25038-54-4, 65997-17-3, 1163-19-5, 1309-64-4 and 138265-88-0Information provided by LG Chemical |
|||
| Flexural Modulus | 8.53 GPa @Thickness 3.20 mm |
1240 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUMID GP2301BF PA 66+GF30%, Flame Retardant Feature: Injection Molding, PA 66+GF30%, Flame RetardantApplication: IT/OA (Micro Switch, ConnectorCAS No. 32131-17-2, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG Che.. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | 5 mm/min; ISO 178 |
| Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Modulus | 8.53 GPa | 1240 ksi | 5 mm/min; ISO 178 |
| Gromax BFG30-FN00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Modulus | 8.52 GPa | 1240 ksi | 5 mm/min; ISO 178 |
| Gromax BFG30-FU00B3 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Modulus | 8.53 GPa | 1240 ksi | 5 mm/min; ISO 178 |
| Gromax BFG30-AS00N1 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp EFP36G PEI LNP* EFP36G is a Polyetherimide base resin containing a Mixed Glass Fiber and PTFE/Silicone.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear (Asia Pacific) LNP* STAT-KON* OEP32 is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON REL33 PA 66 LNP STAT-KON* REL33 is a compound based on Nylon 66 resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66 LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Techmer ES HiFill® PVDF CF15 BK 15% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 15% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Techmer ES HiFill® PVDF CF15-M BK 15% Milled Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Milled Carbon Fiber, 15% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Asia Pacific) LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing Glass Fiber. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WF006U PBT (Asia Pacific) LNP* THERMOCOMP* WF006U is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: UV Stabilized. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA 30% Glass Reinforced PPE+PA Alloy. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
|||
| Flexural Modulus | 8.58 GPa | 1240 ksi | ASTM D 790 |
| SABIC Innovative Plastics LNP Stat-kon DX96690 PC LNP STAT-KON* DX96690 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the America.. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear LNP STAT-KON* OEP32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
| Flexural Modulus | 8.54 GPa | 1240 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WF006U PBT LNP* THERMOCOMP* WF006U is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: UV Stabilized. |
|||
| Flexural Modulus | 8.53 GPa | 1240 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOTUF VF008 Super Tough Nylon LNP THERMOTUF* VF008 is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ISO 178 |
| Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified 33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Westlake Plastics Kynar® PVDF CN-F Polyvinylidene Fluoride (conductive) Non-sloughing carbon-fiber-filled material with resistance to most chemicals and solvents mechanically strong and tough, thermally stable to 335F, flame and abrasion resistant, and easily fabricated.. |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Adell HR-36 30% Glass Reinforced Heat Stabilized PBT |
|||
| Flexural Modulus | 8.55 GPa | 1240 ksi | ISO 178 |
| BASF Ultramid® A3EG6 BK 00564 PA66 (Dry) Information provided by BASF |
|||